1) three-membered boron-nitrogen rings
三元硼氮环
1.
Electronic structure and bonding of three-membered boron-nitrogen rings;
三元硼氮环的电子结构与成键
2) four-membered boron-nitrogen ring
四元硼氮环
3) carbonnitroboriding
碳氮硼三元共渗
4) B-trichloroborazine
三氯环硼氮烷
1.
Synthesis and Characterization of B-trichloroborazine and Polyborazine
三氯环硼氮烷和聚硼氮烷的合成与表征
2.
Crystalline B-trichloroborazine(TCB) was synthesized and purified using Schlenk technique with boron trichloride(BCl3) and ammonium chloride(NH4Cl) as raw materials and chlorobenzene(C6H5Cl) as solvent.
以三氯化硼和氯化铵为原料,以氯苯为溶剂,采用Schlenk技术合成并提纯出高纯度三氯环硼氮烷(TCB)晶体,利用二甲胺与TCB进行反应,得到TCB的衍生物烷基胺环硼氮烷,为获得高质量BN材料作了原料准备。
5) boratranes
杂氮硼三环类化合物
1.
The ultraviolet photoelectron spectroscopy (UPS) of 6 boratranes are recorded.
报道了六种杂氮硼三环类化合物的紫外光电子能谱(UPS)采用RHF/3-21G优化了各分子的优势构型,根据化合物UPS的谱带特征结合RHF/6-31G~*的计算结果对化合物的UPS进行了解析和指认,精确给出了各化合物中σ_(N→B)配键电子的电离峰位置。
6) Borazine
环硼氮烷
1.
DFT Studies on Electronic Spectra and Nonlinear Optical Properties of Symmetric Squaraine Derivatives Linked with Borazine;
六元环硼氮烷对称取代方酸的电子光谱和非线性光学性质的DFT研究
2.
This is a summery of the synthesis, structure and reaction of borazine.
对环硼氮烷的合成、结构和反应进行了综述。
3.
Cured polyborazine was obtained by heating borazine at 80℃ for 72hrs and was converted to BN ceramic after pyrolysis.
以硼氢化锂和硫酸铵为原料合成了氮化硼陶瓷先驱体环硼氮烷,以GC-MS、FT-IR和1H-NMR等方法对其组成和结构进行了表征和确认。
补充资料：碳氮硼三元共渗
分子式：
CAS号：
性质：碳氮硼三元共渗是使钢制工件同时渗入碳、氮、硼三种元素的化学热处理工艺。共渗后渗层的硬度较渗硼为低(HV600～1000)。碳氮硼三元共渗如用于石油机械易损零件，能提高使用寿命。碳氮硼三元共渗后空冷即可得到HV750的硬度，对于上述钢材制造的薄小工件，可以省去淬火工序。碳氮硼三元共渗也可以在气体介质中进行，例如用尿素(2500g)、甲醇(8L)、硼酸三甲酯(5L)、丙酮(6L)的混合渗剂滴入840~860℃的井式渗碳炉中，保温3～5h后，在低碳合金渗碳钢上可得到0.4～0.6mm渗层，表面硬度达HRC63～65，甚至更高。
CAS号：
性质：碳氮硼三元共渗是使钢制工件同时渗入碳、氮、硼三种元素的化学热处理工艺。共渗后渗层的硬度较渗硼为低(HV600～1000)。碳氮硼三元共渗如用于石油机械易损零件，能提高使用寿命。碳氮硼三元共渗后空冷即可得到HV750的硬度，对于上述钢材制造的薄小工件，可以省去淬火工序。碳氮硼三元共渗也可以在气体介质中进行，例如用尿素(2500g)、甲醇(8L)、硼酸三甲酯(5L)、丙酮(6L)的混合渗剂滴入840~860℃的井式渗碳炉中，保温3～5h后，在低碳合金渗碳钢上可得到0.4～0.6mm渗层，表面硬度达HRC63～65，甚至更高。