1) compact strength
压坯强度
1.
Discuss the value S notation of compact strength;
金属粉末压坯强度S值表示法的探讨
2) green strength
坯体强度
1.
Effects of process parameters on the gelcasting green strength and sintered density of stainless steel;
工艺参数对凝胶注模成型不锈钢坯体强度和烧结密度的影响
3) green strength
生坯强度
1.
Comparing with traditional ceramic forming method,gelcasting sample has a higher green strength,which is suitable for machining.
结果表明:在注凝成型体系中,这些物质的相对含量对所成生坯的强度有很大影响,在最佳工艺条件下,氧化铝生坯强度可达到32MPa,完全可以满足机加工要求。
4) strength of single of adobe
土坯强度
6) green density
压坯密度
1.
Warm compaction behavior of 316L stainless steel was investigated, influences of processing parameters of warm compaction on green density of 316L stainless steel were studied.
研究316L不锈钢的温压行为,分析温压工艺参数对压坯密度的影响。
2.
It is found that the green density and sintered density of YBa_2Cu_3O_(7-δ) powders with different granularity varied differently with the variation of pressure.
结果表明,不同粒度YBaCuO超导粉体的压坯密度、烧结密度(即烧结前后的致密度)随压力的变化规律不同。
3.
Influences of processing parameters of warm compaction on green density of 420 stainless steel were studied.
对420不锈钢粉末进行温压,探索温压工艺参数对压坯密度的影响,并对温压与室温模压(添加0。
补充资料：干坯强度
分子式：
CAS号：
性质：表不泥坯干燥后对弯曲负荷的抵抗能力，以MPa为单位。生坯必须具有足够的干燥强度，才能保证修坯、上釉、装窑等工序顺利进行，才能减少破损。原生黏土(如高岭土)虽比较纯，但结合能力差，配制成的坯体的生坯强度比较低。在实际生产中通常加入一部分次生黏土(可塑性比较大的黏土)以提高生坯强度。在特种陶瓷配料中，绝大多数原料不具可塑性，为保证其具有足够的干坯强度，常在配料中添加一定的有机黏结剂，如聚乙烯醇、聚醋酸乙烯酯、聚苯乙烯、甲基纤维素、糊精等。
CAS号：
性质：表不泥坯干燥后对弯曲负荷的抵抗能力，以MPa为单位。生坯必须具有足够的干燥强度，才能保证修坯、上釉、装窑等工序顺利进行，才能减少破损。原生黏土(如高岭土)虽比较纯，但结合能力差，配制成的坯体的生坯强度比较低。在实际生产中通常加入一部分次生黏土(可塑性比较大的黏土)以提高生坯强度。在特种陶瓷配料中，绝大多数原料不具可塑性，为保证其具有足够的干坯强度，常在配料中添加一定的有机黏结剂，如聚乙烯醇、聚醋酸乙烯酯、聚苯乙烯、甲基纤维素、糊精等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。