您的位置：首页 -> 词典 -> 磺化聚苯乙烯离聚体
1)  sulfonated polystyrene ionomer
磺化聚苯乙烯离聚体
1.
Sulfonated polystyrene ionomers are used as compatibilizers for PA1010/HIPS blendings and their effects on the structure and mechanical properties of final products were observed by means of a SEM,DMA,polarized optical microscope and impact testings.
用磺化聚苯乙烯离聚体增容ＰＡ１０１０／ＨＩＰＳ共混体系，通过ＳＥＭ、ＤＭＡ、偏光显微镜和冲击试验考察了离聚体对ＰＡ１０１０／ＨＩＰＳ体系结构与性能的影响。
2)  sulfonic polystyrene
聚阴离子磺化聚苯乙烯
3)  zinc salt of sulfonated polystyrene ionomer
磺化聚苯乙烯锌盐离聚体
4)  sulphonated polystyrene sodium ionomer
磺化聚苯乙烯钠盐离聚体
5)  sulfonated polystyrene
磺化聚苯乙烯
1.
The sulfonated polystyrene (SPS) has been prepared by sulfonation reaction of the polystyrene, which is used as a filtrate reducer for oil well cement slurry.
通过磺化改性,制备了磺化聚苯乙烯(SPS)作为油井水泥降失水剂。
2.
Water borne emulsions of lightly sulfonated polystyrene ionomer(SPS) were prepared by phase inversion technique.
将聚苯乙烯磺化制成聚苯乙烯离聚体 (SPS) ,利用相反转技术 ,将磺化聚苯乙烯离聚体制成具有纳米级稳定的水基微乳液 ,利用 SPS微粒核为反应场所 ,引发另一单体 MMA聚合 ,制备具有相互缠结结构的 PMMA/ SPS复合水基微乳液。
3.
The complexation behavior of sulfonated polystyrene (SPS) containing 9.
采用粘度，差示扫描量热法研究了磺化聚苯乙烯（ＳＰＳ）与甲基丙烯酸甲酯－４－乙烯基吡啶共聚物（ＭＭＡ４ＶＰ）所形成的离子复合物。
更多例句>>
6)  SPS
磺化聚苯乙烯
1.
In this work, the polystyrene was modified to sulfonated polystyrene ionomer(SPS) and was emulsified to a stable polymer waterborne emulsion by using the technology of phase inversion.
将聚苯乙烯制成磺化聚苯乙烯离聚体,利用相反转技术,将磺化聚苯乙烯离聚体制成具有纳米级稳定的水基微乳液,利用磺化聚苯乙烯颗粒内部作为反应场所,引发另一单体丙烯酸丁酯聚合,制备聚丙烯酸丁酯/磺化聚苯乙烯复合水基微乳液。
2.
The polystyrene was modified to sulfonated polystyrene ionomer (SPS) which was emulsified to waterborne emulsion by using the technology of phase inversion.
利用相反转技术制备磺化聚苯乙烯(SPS)水基微乳液,研究发现,通过选择溶剂和控制混合溶剂的组成,可制备不同颗粒形态结构的SPS水基微乳液,并研究了相反转过程、乳液稳定性与混合溶剂组成之间的关系。
3.
he morphology and thermal property of sulfonated polystyrene (SPS) and its ionomers were studied through DSC, DMA, TEM, SAXS and TGA.
通过ＤＳＣ、ＤＭＡ、ＴＥＭ、ＳＡＸＳ和ＴＧ对ＳＰＳ（磺化聚苯乙烯）及其离聚体的形态结构和热性能进行了研究。
更多例句>>
补充资料：聚氯乙烯离聚物
分子式：
CAS号：

性质：是大分子链上含有离子键的一种聚氯乙烯共聚物。和一般聚氯乙烯相比，耐热性，机械强度都明显提高。玻璃化温度64.7℃。由氯乙烯与邻苯二甲酸单(丙烯酰氧乙基)酯进行悬浮共聚得到含羧基产品，再用金属氧化物中和而得。用于制作耐热制品。

说明：补充资料仅用于学习参考，请勿用于其它任何用途。