1) modified zirconium oxide
改性氧化锆
1.
A new technique employing modified zirconium oxide to replace the concentrated sulfuric acid as catalyst in synthesis butyl lactate is studied.
对以改性氧化锆替代传统的浓硫酸作酯化反应催化剂合成乳酸丁酯的新工艺进行了试验探索，取得了满意效果，合格产品收率达８５％以上。
2.
A new technique employing modified zirconium oxide to replace the concentrated sulfuric acid as catalyst in synthesis ethyl lactate is studied.
对以改性氧化锆替代传统的浓硫酸作酯化反应催化剂合成乳酸乙酯的工艺进行了试验探索。
2) stabilized zirconium dioxide
稳定性二氧化锆
1.
Application,development and preparation of stabilized zirconium dioxide in refractory material and special ceramics are stated.
综述了稳定性二氧化锆在耐火材料及特种陶瓷领域的应用、发展及制备方
3) stable zirconium oxide
稳定性氧化锆
4) oxidizing modification
氧化改性
1.
Characterization and coagulation performance of poly-silicic-ferric sulfate and its oxidizing modification coagulant;
聚硅酸铁及其氧化改性剂的表征与性能分析
5) oxidative modification
氧化改性
1.
The oxidative modification process of calcium lignosulfonate(CLS) was studied.
研究了木素磺酸钙 (简称木钙 )的氧化改性工艺 ,比较了几种氧化剂与木钙反应后性能的差异。
补充资料：氧化锆-氧化钇红外陶瓷
分子式： ZrO2-Y2O3
CAS号：
性质：一种以二氧化锆为基体固溶6％～8％(mol)氧化钇的红外光学材料。立方晶结构。熔点2700℃。密度5.98g/cm3。红外透射波段1～10μm。采用1450℃以上高温烧结或1300～1700℃，50～300MPa热压制取。用于制造耐高温红外窗口和整流罩。
CAS号：
性质：一种以二氧化锆为基体固溶6％～8％(mol)氧化钇的红外光学材料。立方晶结构。熔点2700℃。密度5.98g/cm3。红外透射波段1～10μm。采用1450℃以上高温烧结或1300～1700℃，50～300MPa热压制取。用于制造耐高温红外窗口和整流罩。