1) carbonaceous gold ore
碳质金矿
1.
Enhancement of cyanide leaching rate of carbonaceous gold ores by efficient passivation Process;
高效抑制技术提高碳质金矿石浸出率（连载）
2.
The Promotion and inhibition of the success of CIL─study on high gold extraction percentage by cyanide leaching of carbonaceous gold ore;
抑制和促进的CIL－碳质金矿高收率氰化冶炼工艺研究
2) carbon-bearing gold ore
碳质金矿石
1.
Researches on carbon-bearing gold ore treatment with microwave;
微波处理碳质金矿石技术研究
3) high-carbon gold ore
高碳质金矿石
1.
Experimental research on gold recovery from high-carbon gold ore with gravity concentration;
重选法回收某高碳质金矿石中金的试验研究
4) refractory carbonaceous gold ore
碳质难处理金矿
1.
A process Ieaching gold from a refractory carbonaceous gold ores with hypochlorous solution was proposed.
论述了碳质金矿的矿物学特性 ,次氯酸钠氯化法直接浸出碳质微细粒浸染型难处理金矿的工艺过程和操作条件 ,讨论了不同因素对浸出过程的影响 ,评述了水溶液氯化法浸取贵州某碳质难处理金矿的试验结
5) carbonaceous silver ore
碳质银矿
6) gold concentrate containing carbon
含碳金精矿
补充资料：铝碳质整体塞棒
铝碳质整体塞棒
alumina graphite monolithic stopper
IUtanzhi zhengti sa}bdng铝碳质整体塞棒(alumina graphite monoli-thicst叩per)以刚玉和鳞片状石姜为主要原料烧成的控制钢液流量的耐火制品。其特点是整体性好，代替了由传统的袖砖和塞头组装的塞棒，使用更安全，而且还可以通过塞棒向中间罐水口吹氢，净化钢水，防止水口堵塞。 铝碳质整体塞棒的理化指标:A120360%，F·C25%，体积密度2.359/c m3，显气孔率13%，耐压强度14.7MPa，抗折强度(1400℃)5.oMPa，线膨胀率(1000℃)。.5%。其制造工艺是将刚玉、石墨和添加剂等原料按配比称量，以酚醛树脂为结合剂，经混练，用等静压机成型。半成品经干燥后，在无氧化烧成窑内烧成。最后，经X射线无损探伤、车床加工、喷涂防氧化涂层等工序，经检验合格后为成品。铝碳质整体塞棒的工艺流程见图。 刚玉石墨添加剂福猛啮~遍州画画趣画莎甲’ 成品 铝碳质整体塞棒的生产工艺流程 在制造中，配料要准确，原料要符合工艺要求，泥料必须造粒，成型压力为120~150MPa，烧成温度为1000~1350℃。 该制品安装于连铸机中间罐内，用其开启程度来控制钢水流量的大小.要求干燥贮存，使用前必须预热。 (周川生)