1) RE Medium Manganese White Cast Iron
稀土中锰白口铁
2) RE white cast iron
稀土白口铁
3) medium manganese white cast iron
中锰白口铸铁
1.
It is possible to change the shape and distribution of carbides in medium manganese white cast iron and make them change from network into semi network,streaky and blocky structure,eliminating cast defects,refining the structure and enhancing strength and toughness greatly.
采用变质处理、热塑性变形和热处理 3种工艺可以改变中锰白口铸铁碳化物的形态和分布。
2.
In different wear situations , the effect of residual austenite (γR) on abrasion resistance of medium manganese white cast iron was investigated.
研究了在不同磨损工况中残余奥氏体(γR)对中锰白口铸铁抗磨性的影响。
4) low-chromium white cast iron with RE
低铬稀土白口铸铁
1.
Vanes of peening machine used for cleaning castings are made of low-chromium white cast iron with RE.
用于清理铸件的抛丸机叶片材料为低铬稀土白口铸铁,淬火后不回火的叶片的使用寿命比经淬火、回火的叶片提高了15~20 h,从而缩短了热处理周期,节约了能源,提高了经济效益。
5) Medium manganese rare-earth magnesium cast ball
中锰稀土镁铸球
6) high Cr-Mn white cast iron
高铬锰白口铸铁
1.
The effects of V on the microstructures and properties of high Cr-Mn white cast iron was Investigated in this paper.
探讨了钒以及热处理工艺对高铬锰白口铸铁组织和性能的影响。
补充资料：中锰球铁
分子式：
CAS号：
性质：铸态使用的马氏体球铁。化学成分为(％)：C3.3～3.8，Si3.3～4.5，Mn5.0～7.0，P<0.15，S<0.02，Mg0.03～0.06，RE0.03～0.05。中锰球铁以冲天炉熔化，经球化和孕育处理即能得到中锰球铁。其组织为：球状石墨+共晶碳化物+马氏体+残留奥氏体，硬度约为HRC48～56。这种铸铁生产工艺简单，成本低廉，主要用作球磨机磨球。中锰球铁不宜用于冲击大的场合，否则会发生剥落和碎裂。
CAS号：
性质：铸态使用的马氏体球铁。化学成分为(％)：C3.3～3.8，Si3.3～4.5，Mn5.0～7.0，P<0.15，S<0.02，Mg0.03～0.06，RE0.03～0.05。中锰球铁以冲天炉熔化，经球化和孕育处理即能得到中锰球铁。其组织为：球状石墨+共晶碳化物+马氏体+残留奥氏体，硬度约为HRC48～56。这种铸铁生产工艺简单，成本低廉，主要用作球磨机磨球。中锰球铁不宜用于冲击大的场合，否则会发生剥落和碎裂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。