1) Cr-Mn-Cu alloy white cast iron
铬锰铜合金白口铸铁
1.
The wear resistance of Cr-Mn-Cu alloy white cast iron after heat treatment was studied and compared with that of as-cast Cr-Mn-Cu alloy white cast iron,the wear failure mechanism and microstructure on the wear end surface and nonwear end surface were analyzed.
以铬锰铜合金白口铸铁的铸态材料为对比材料,考察了热处理后的铬锰铜合金白口铸铁材料的耐磨性能,对试验材料的磨损失效机理和磨损端面与无磨损端面的金相组织进行了分析。
2.
The wearing resistance,microstructure,worn surface morphology and hardness change in wearing end-face and non-wearing end-face of Cr-Mn-Cu alloy white cast iron were tested and analyzed.
对铬锰铜合金白口铸铁的耐磨性、无磨损端面及磨损端面的微观组织、磨损形貌及硬度进行了试验和分析。
3.
The erosive-wear resistance of heat treated Cr-Mn-Cu alloy white cast iron was investigated compared with that of as-cast one, and the impact fractures,the erosive-wear resistant failure mechanism and the section metallurgical structure of the test materials were analyzed.
以铸态铬锰铜合金白口铸铁为对比材料,考察了热处理后的铬锰铜合金白口铸铁的抗冲蚀磨损性能,并对试验材料的冲击断口形貌、抗冲蚀磨损失效机理和冲蚀磨损横切面的金相组织进行了分析。
2) high Cr-Mn white cast iron
高铬锰白口铸铁
1.
The effects of V on the microstructures and properties of high Cr-Mn white cast iron was Investigated in this paper.
探讨了钒以及热处理工艺对高铬锰白口铸铁组织和性能的影响。
3) manganese alloy wear-resistance
锰合金白口耐磨铸铁
4) forged medium-chromium ally white cast iron
锻造中铬合金白口铸铁
5) high chromium nickel alloyed white cast irons
高铬镍合金白口铸铁
6) Low-chromium alloted white cast lron Grinding balls
低铬合金白口铸铁磨球
补充资料：白口铸铁
在结晶凝固过程中没有石墨析出，断口呈银白色的铸铁。它含有较多的游离渗碳体，所以具有很高的硬度（一般在HB 500以上），但性脆。多用于抗磨损的零件，例如农具、磨球、磨煤机零件、抛丸叶片、泥浆泵零件、铸砂管以及冷硬轧辊的外表层等。以含碳量2.6～3.8％、含硅量0.6～0.9％、含锰量0.2～0.8％的铁水，加快铸件凝固过程，或加入强烈形成碳化物的金属元素的方法，可得白口铸铁件。中国早在春秋晚期已经使用白口铸铁（见冶金史）。