1.
Semi-solid isothermal treatment is thought as a potential technology in the manufacturing non-dendritic structure alloy slurry, the research of this technology is helpful to rich the theory of semi-solid metal forming and accelerate the application of this technology.
在半固态等温热处理制备非枝晶组织合金坯料已取得研究成果的基础上,回顾了该技术在工艺因素对非枝晶组织形成的影响、非枝晶组织的形成机理和非枝晶组织坯料的压缩变形特性等方面的研究进展,指出了该技术目前在这些方面还存在的问题,并展望了今后的发展方向。
3) wrought magnesium alloy billets
变形镁合金坯料
1.
Preparation of high purity of AZ31B wrought magnesium alloy billets with large size;
大规格AZ31B变形镁合金坯料的高纯净化制备
4) AlSi7Mg alloy slurry
AlSi7Mg合金坯
5) GH536 alloy's tube blank
GH536合金管坯
1.
Through analyzing the surface micro-cracks of GH536 alloy's tube blank produced by the Steel Pipe Company in this paper,the authors discovered that the cracks were classified as transcrystalline cracks with a depth of 0.
通过对钢管公司生产的GH536合金管坯表面微裂纹的分析发现,表面裂纹属于穿晶裂纹,深度仅0。
6) aluminium alloy ingot
铝合金锭坯
补充资料：LSI法
具体操作步骤
具有应收外汇账款的公司，在征得债务方同意后，以一定折扣为条件提前收回货款（以此消除时间风险）；并通过在即期外汇市场上将外汇兑换成本币（以此消除价值风险）；然后，将换回的本币进行投资，所获的收益用以抵补因提前收汇的折扣损失。
[编辑]LSI法在应付帐款中的运用
例如，德国的D公司90天后有一笔US$100 000的应收贷款。为防止届时美元贬值给公司带来损失，该公司征得美国进口商的同意，在给其一定付现折扣的情况下，要求其在2天内付清款项（暂不考虑折扣数额）。D公司提前取得美元货款后，立即进行即期外汇交易，外汇市场的即期汇率为US$1=DMl.6670÷1.6680。随即D公司用兑换回的本币 DMl66 700进行90天的投资（暂不考虑利息因素）。
图1
由图1可见，通过提前收付，消除了时间风险，通过即期外汇交易，把美元变成等价值本币，又消除了价值风险。以本币进行投资，将来不再有真正的外汇流动，仅有一笔本币的回收。
同上例，E公司也可以采用LSI法避险。设即期外汇市场汇率仍为US$1=1.6310÷1.6340，则其操作步骤如下，先从银行借款（borrow），即借入相应的本币81 700马克，再与银行签定即期合同（spot），即用8l 700马克购买50 000美元：最后再提早支付（1ead），即从债权人处获得一定折扣的前提下提前付款。从这个程序看，应该是borrow-spot-lead，但国际交易中，习惯上人们仍把其称为LSI法，而不叫做BSL法。
图2
由图2看出，通过借本币、换外币及提前支付外币应付账款，风险全部消除。未来只有一笔本币借款需要偿还，借款的利息损失，尚可在提前偿付货款时从出口商处获得的折扣中予以部分冲抵。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条