1) EVA Latex Particles
EVA乳胶粒
2) PSA-A latex
PSA-A乳胶粒
1.
In this paper,anionic PSA-A latex particles can be coated with hydrate CeO2 by aging the solution containing PSA-A,urea,and Ce(SO4)2.
以PSA-A乳胶粒为模板,通过硫酸高铈和尿素的水解反应得到PSA/水合CeO2的核/壳结构的复合微球,通过煅烧除去乳胶粒模板得到立方相CeO2空心微球。
3) latex particle
乳胶粒子
1.
Calculation of force acting on flexing and deforming latex particle in oil
油液对伸缩变形乳胶粒子作用力的计算
2.
The fundamental morphologies of core/shell latex particle and common characterization methods were presented.
介绍了核壳型乳胶粒子的基本形态结构和常用的表征手段,详细说明了用透射电子显微镜(TEM)表征核壳型乳胶粒子结构的两种情况,即分析透射电子显微镜法、普通透射电子显微镜法(免染色法和选择性染色法),并给出了它们的适用范围。
3.
It is found that the latex particle has core-shell structure, the glass transition temperat.
透射电镜观察证实了此乳胶粒子的形态特征,表征了共聚物的玻璃化转变温度及薄膜的拉伸强度和吸水率。
4) latex particle
乳胶粒
1.
Through the analysis of ultraviolet spectroscopy, it is found out that the absorbance of the latex particles is highe.
通过“粒子设计”利用核壳乳液聚合技术以功能型紫外线吸收剖、苯乙烯、丙烯酸丁酯、甲基丙烯酸甲酯、丙烯酸乙酯为单体制备出核壳结构的聚合物乳胶粒。
2.
The mechanism of latex particle formation and its transformation during anionic emulsion polymerization was studied, while DBSA was used as catalyst and emulsifier.
分析实验现象发现,该体系中羟基硅油乳胶粒是通过胶束和单体珠滴两种方式形成的,由单体珠滴生成的体积较大的羟基硅油乳胶粒是形成羟基硅油乳液“漂油”的主要原因。
3.
The occupied area (Am)of a sodium dodecyl benzene sulphonate(SDBS) molecule adsorbed on PEA latex particles and the covered area ratio on particle surfaces under various surfactant contents were measured.
测定了乳化剂十二烷基苯磺酸钠(SDBS)分子在聚丙烯酸乙酯(PEA)乳胶粒表面的覆盖面积A_m和不同乳化剂用量下胶乳的表面覆盖率φ。
5) latex particle size
乳胶粒径
1.
The effects of amount and composition of composite emulsifiers and of redox initiators on latex particle size were discussed by orthogonal experiment and homogeneous design experiment respectively.
研究了醋酸乙烯酯 /丙烯酸丁酯 /丙烯酸三元共聚合乳液的合成工艺条件 ,应用正交实验和均匀实验设计得出了乳化剂用量及配比 ,氧化 -还原引发剂用量及配比对乳胶粒径的影响 ,乳化剂及体系 p H值对乳液稳定性的影响 ;采用间歇法聚合工艺 ,当乳化剂用量为 7。
6) latex particles
乳胶粒子
1.
P(St-BA-AA) nano-micropore latex particles were step to step treated with alkali and acid at high temperature(90 ℃) in the first time.
通过分步调节碱和酸度,并在高温条件(90℃)下进行酸碱处理,首次制得P(St-BA-AA)三元共聚物纳米微孔乳胶粒子。
补充资料：乳胶
| 乳胶 latex 泛指聚合物微粒分散于水中形成的胶体乳液。又称胶乳。习惯上将橡胶微粒的水分散体称为胶乳，而将树脂微粒的水分散体称为乳液。以乳胶为原料制成的制品称乳胶制品，常见的如海绵、手套、玩具、胶管等。 乳胶可分为天然、合成和人造3类 。①天然乳胶是橡胶树割胶时流出的液体，呈乳白色，固含量为30％～40％，橡胶粒径平均为1.06微米。新鲜的天然乳胶含橡胶成分27％～41.3％(质量)、水44％～70％、蛋白质0.2％～4.5％、天然树脂2％～5％、糖类0.36％～4.2％、灰分0.4％。为防止天然乳胶因微生物、酶的作用而凝固，常加入氨和其他稳定剂。天然乳胶主要用于制作海绵制品、压出制品和浸渍制品。②合成乳胶一般通过乳液聚合制得，如聚丁二烯乳胶、丁苯乳胶等。为使固含量达到40％～70％，首先使橡胶微粒附聚成较大的颗粒，再采用与天然乳胶相似的方法浓缩。合成乳胶主要用于地毯、造纸、纺织、印刷、涂料及胶粘剂等工业部门。③人造乳胶是一种非乳液聚合的橡胶乳胶。向溶液聚合生成的胶体中加入水和表面活性剂，使橡胶微粒分散于水中，然后蒸除溶剂制得。如果橡胶不能充分溶解于溶剂中，可将生胶和胶料在含有乳化剂的水相存在的条件下，不断捏炼，直至形成稳定的橡胶水分散体。人造乳胶与合成乳胶的用途基本相同。 |