1) warm water crosslinking
温水交联
1.
Warm water crosslinking performance and influence factors of shielded layer of warm water crosslinking cable were investigated.
研究适用于温水交联电缆的屏蔽层的温水交联性能及其影响因素。
2) warm water silane crosslinking
温水硅烷交联
1.
peroxide(DCP) crosslinking,warm water silane crosslinking and warm-water-free silane crosslinking,are used.
生产中压交联聚乙烯电力电缆,可以采用过氧化物(DCP)交联、温水硅烷交联和免水煮硅烷交联等三种交联方法,本文对这三种交联方式的投资价值进行了比较分析,认为硅烷交联特别是免水煮硅烷交联,是企业生产中压交联电缆投资最少的交联方式。
3) Warm water silane-closslinked PE
温水交联聚乙烯
4) water-crosslinkable polymer
温水交联聚合物
5) cross-linking at room temperature
室温交联
1.
In this paper first a polyacrylamide with low molecular weight was synthesized,then the polyacrylamide was hydroxymethylated with formaldehyde,finally the hydroxymethylatcd polyacrylamide and acrylamidc reacted to form the cross-linking at room temperature polyacrylamide.
首先合成低分子量的聚丙烯酰胺,再用甲醛使其羟甲基化,最后羟甲基化聚丙烯酰胺和丙烯酰胺缩合得到可室温交联的聚丙烯酰胺。
补充资料：Tm-002硅烷交联剂
1. 化学名称
甲基三乙酰氧基硅烷
2. 物理性质
无色至浅黄色透明液体，较低温度下可转变为白色晶体。易吸湿，可溶于醋酸酐，遇水会交联，并产生醋酸。
3. 技术规格
外观 无色至浅黄色透明液体，或白色晶体
密度（r25）g/cm3 1.1750~ 1.1800g/cm3
含量（%） ≥95
折射率(n 25d) 1.4050±0.0005
沸点（℃） 110-112/17mmhg
熔点（℃） 40.5
cl-（%） ≤0.1
4. 用途
本品主要用作室温硫化硅橡胶的交联剂。
5. 包装与储运
塑料桶包装，每桶净重10kg、25kg、100kg、180kg。密封储存于阴凉、干燥通风处，防潮防水，远离火种、热源。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。