1) TiB 2 Ni ceramet
TiB_2-Ni金属陶瓷
2) Al2O3/Ni cermet
Al2O3/Ni金属陶瓷
1.
Al2O3/Ni cermet were prepared by hot pressing,and the relationship between their microstructure,mechanical and dielectric properties with Ni particle content were investigated.
以热压烧结的方法制备了Al2O3/Ni金属陶瓷,探讨了Al2O3/Ni金属陶瓷显微结构、力学性能及微波介电性能随Ni粒子含量变化的规律。
2.
Ni coated α-Al2O3 composite microspheres are first synthesized by heterogeneous precipitation coating method, and then Al2O3/Ni cermets are prepared by hot press-sintering of the as-prepared Ni-coated α-Al2O3 powders.
首先采用非均相沉淀包裹法制备金属镍包裹α-Al2O3复合微球粉体,然后采用热压烧结制备了Al2O3/Ni金属陶瓷。
3) Al_2O_3/Ni cermet
Al_2O_3/Ni金属陶瓷
1.
The powders were sintered by hot-pressing, and Al_2O_3/Ni cermet obtained.
采用包裹工艺和热压工艺制备了Al_2O_3/Ni金属陶瓷。
4) TiC-Ni cermets
TiC-Ni金属陶瓷
1.
TiC-Ni cermets were prepared by combining forced compaction and self-propagating high-temperature synthesis (SHS).
利用自蔓延高温燃烧合成结合机械压力方法制备了TiC -Ni金属陶瓷 ,研究了TiC-Ni金属陶瓷材料的热膨胀性质随温度和组成的变化关系。
5) TiC-Ni ceramet
TiC-Ni基金属陶瓷
补充资料：含二氧化硅金属陶瓷
分子式：
CAS号：
性质：由二氧化硅陶瓷和金属或合金组成的复合材料。二氧化硅呈颗粒状，粒度200目，通常还加人体积含量为2%～7%的氧化铝，基体金属通常由铜、锌、锡、铅、铁等组成，同时加入弥散的石墨为润滑剂。采用粉末冶金技术制造。主要用作离合器和刹车装置等的摩擦材料。