1) temper brittleness
回火脆
1.
The results showed that the fracture of shifting handle were mainly intergranular fracture which happened because some parts peoduced the temper brittleness during high-frequent heat treatment and the material was brittled,then brittle fracture had happened at the late bonderite process.
结果表明 :活动拨柄的断裂主要是沿晶断裂 ,引起沿晶断裂的原因主要是活动拨柄局部高频热处理时产生一类回火脆 ,致使材料局部出现脆化 ,在后续的磷化处理过程中发生脆断。
2.
The experimental study shows that the temper brittleness temperature is about 330℃.
本文对910装甲钢在890℃淬火,不同温度下回火下的力学性能进行了试验研究,试验表明其回火脆性温度为330℃左右。
2) temper embrittlement
回火脆化
1.
A Study on Temper Embrittlement Overaging Phenomenon of Alloy Steel 2.25Cr-1Mo;
2.25Cr-1Mo合金钢回火脆化过时效现象的研究
2.
Development of the kinetics model of temper embrittlement for hydrogenation reactors;
加氢反应器回火脆化动力学模型
3.
Electrochemical reverse polarization method for temper embrittlement checking of turbine rotor steel;
电化学反向极化法检测汽轮机转子回火脆化的研究
3) temper brittleness
回火脆性
1.
The investigation shows that this defect arises from temper brittleness of the steel.
试验表明,其原因是钢的回火脆性所致。
2.
The cold crack sensitiveness and temper brittleness of three pressure vessel steels for high temperature,high pressure and hydrogen environment were compared and analyzed in this article.
分析比较了214 Cr-1Mo,214 Cr-1Mo-14 V和3Cr-1Mo-14 V三种高温高压临氢压力容器用钢的冷裂敏感性和回火脆性,提出了对热壁加氢反应器的选材建
3.
Cr Mo steel's temper brittleness is expounded,the affecting factors of temper brittleness of 21/4 Cr 1Mo steel in hydrogenated reactor are analyzed.
全面阐明了铬钼钢回火脆性的基本概念 ,分析了加氢反应器用 2 Cr- 1 Mo钢回火脆性的影响因素 ,指出了防止回火脆性破坏应采取的措施。
4) Temper Embrittlement
回火脆性
1.
Influence of Applied Stress on Temper Embrittlement of 2.25Cr-1Mo Alloy Steel;
作用应力对2.25Cr-1Mo合金钢回火脆性的影响
2.
Study of reverse temper embrittlement NGS mechanism in steel 12Cr1MoV;
12Cr1 MoV钢的可逆回火脆性非平衡晶界偏聚机制研究
3.
Temper Embrittlement of Steels for Heavy Forging;
大型锻件用钢的回火脆性
5) Reverse temper embrittlement
逆回火脆
1.
Further investigation shows this phenomenon is typical reverse temper embrittlement (RTE) effect.
实验显示服役后材料的脆化是可逆的,属于逆回火脆现象。
6) temper brittleness
回火脆性;驯脆
补充资料：回火脆性
见回火。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。