1) appraising and controlling of temper brittleness
回火脆性评定、控制
2) temper brittleness
回火脆性
1.
The investigation shows that this defect arises from temper brittleness of the steel.
试验表明,其原因是钢的回火脆性所致。
2.
The cold crack sensitiveness and temper brittleness of three pressure vessel steels for high temperature,high pressure and hydrogen environment were compared and analyzed in this article.
分析比较了214 Cr-1Mo,214 Cr-1Mo-14 V和3Cr-1Mo-14 V三种高温高压临氢压力容器用钢的冷裂敏感性和回火脆性,提出了对热壁加氢反应器的选材建
3.
Cr Mo steel's temper brittleness is expounded,the affecting factors of temper brittleness of 21/4 Cr 1Mo steel in hydrogenated reactor are analyzed.
全面阐明了铬钼钢回火脆性的基本概念 ,分析了加氢反应器用 2 Cr- 1 Mo钢回火脆性的影响因素 ,指出了防止回火脆性破坏应采取的措施。
3) Temper Embrittlement
回火脆性
1.
Influence of Applied Stress on Temper Embrittlement of 2.25Cr-1Mo Alloy Steel;
作用应力对2.25Cr-1Mo合金钢回火脆性的影响
2.
Study of reverse temper embrittlement NGS mechanism in steel 12Cr1MoV;
12Cr1 MoV钢的可逆回火脆性非平衡晶界偏聚机制研究
3.
Temper Embrittlement of Steels for Heavy Forging;
大型锻件用钢的回火脆性
4) temper brittleness
回火脆性;驯脆
5) sensitivity to tempered embrittlement
回火脆性敏感性
补充资料：回火
| 回火 tempering 将经过淬火的工件重新加热到低于下临界温度的适当温度，保温一段时间后在空气或水、油等介质中冷却的金属热处理。钢铁工件在淬火后具有以下特点：①得到了马氏体、贝氏体、残余奥氏体等不平衡（即不稳定）组织。②存在较大内应力。③力学性能不能满足要求。因此，钢铁工件淬火后一般都要经过回火。 作用 回火的作用在于：①提高组织稳定性，使工件在使用过程中不再发生组织转变，从而使工件几何尺寸和性能保持稳定。②消除内应力，以便改善工件的使用性能并稳定工件几何尺寸。③调整钢铁的力学性能以满足使用要求。 回火之所以具有这些作用，是因为温度升高时，原子活动能力增强，钢铁中的铁、碳和其他合金元素的原子可以较快地进行扩散，实现原子的重新排列组合，从而使不稳定的不平衡组织逐步转变为稳定的平衡组织。内应力的消除还与温度升高时金属强度降低有关。一般钢铁回火时，硬度和强度下降，塑性提高。回火温度越高，这些力学性能的变化越大。有些合金元素含量较高的合金钢，在某一温度范围回火时，会析出一些颗粒细小的金属化合物，使强度和硬度上升。这种现象称为二次硬化。 要求 用途不同的工件应在不同温度下回火，以满足使用中的要求。①刀具、轴承、渗碳淬火零件、表面淬火零件通常在250℃以下进行低温回火。低温回火后硬度变化不大，内应力减小，韧性稍有提高。②弹簧在350～500℃下中温回火，可获得较高的弹性和必要的韧性。③中碳结构钢制作的零件通常在500～600℃进行高温回火，以获得适宜的强度与韧性的良好配合。淬火加高温回火的热处理工艺总称为调质。 钢在300℃左右回火时，常使其脆性增大，这种现象称为第一类回火脆性。一般不应在这个温度区间回火。某些中碳合金结构钢在高温回火后，如果缓慢冷至室温，也易于变脆。这种现象称为第二类回火脆性。在钢中加入钼，或回火时在油或水中冷却，都可以防止第二类回火脆性。将第二类回火脆性的钢重新加热至原来的回火温度，便可以消除这种脆性。 |