1) borocarbon phase
碳硼相
1.
The borocarbon phase is analyzed synthetically for 60Si 2MnREB spring steel by applying the microsize analysis with the use of X ray diffraction and electron probe.
使用X射线衍射和电子探针微区分析方法对 6 0Si2 MnREB弹簧钢中的碳硼相进行了综合分析 。
2) silicon carbide-titanium diboride composites
碳化硅-硼化钛复相陶瓷
3) boron phase
硼相
1.
The results show that,when cooling rate is above 10℃/s,martensite structure will be obtained,and boron phase will be precipitated at grain boundary,but disappear when cooling rate is above 20℃/s.
结果表明,当冷速大于10℃/s时,就能得到完全的马氏体组织,但此时晶界会有"硼相"析出,冷速为20℃/s以上时,"硼相"消失。
2.
The results show that the cause of boron brittleness is the precipitation of boron phases.
试验证明 ,形成“硼脆”的原因是“硼相”。
4) boron constituent
硼相
5) Boron Carbide
碳化硼
1.
The Development of Pressureless-Sintered Boron Carbide;
无压烧结碳化硼的研究进展
2.
Modification of boron carbide and its application in the silicone coating;
碳化硼的改性及其在有机硅树脂中的应用
3.
Precision grinding of bearing outer jacket made of boron carbide with diamond wheel;
金刚石砂轮加工碳化硼轴承外套的研究
6) boron carbide powders
碳化硼粉
1.
Preparation of boron carbide powders with high tap density;
高振实密度碳化硼粉的制备
补充资料：高硼低碳高温合金
分子式：
CAS号：
性质：一种镍基铸造高温合金。硼含量为0.05％～0.2％，碳含量小于0.05％，不同于普通铸造镍基合金的硼为0.005％～0.03％和碳为0.1％～0.25％。高硼低碳高温合金在保持普通镍基铸造高温合金高温强度的同时，中温性能特别是塑性显著提高，如Mar-M200合金在980℃时具有很高的持久强度、蠕变强度和良好的塑性，但760℃的持久塑性几乎为零，而其改型的高硼低碳B-1950合金在保持Mar-M200合金980℃优越性能的同时，760℃的持久塑性可达2％～5％。主要用于制做发动机涡轮叶片和整体铸造涡轮转子。
CAS号：
性质：一种镍基铸造高温合金。硼含量为0.05％～0.2％，碳含量小于0.05％，不同于普通铸造镍基合金的硼为0.005％～0.03％和碳为0.1％～0.25％。高硼低碳高温合金在保持普通镍基铸造高温合金高温强度的同时，中温性能特别是塑性显著提高，如Mar-M200合金在980℃时具有很高的持久强度、蠕变强度和良好的塑性，但760℃的持久塑性几乎为零，而其改型的高硼低碳B-1950合金在保持Mar-M200合金980℃优越性能的同时，760℃的持久塑性可达2％～5％。主要用于制做发动机涡轮叶片和整体铸造涡轮转子。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。