1) sphere-like α phase
近球形α相
1.
A large number of sphere-like α phases have firstly been found in microstructure of semisolid hypereutectic Al-Si alloy prepared by electromagnetic stirring.
在电磁搅拌法制备的半固态过共晶Ａｌ－Ｓｉ合金的微观组织中发现了大量的近球形α相，实验证明，这种近球形α相是在共晶温度５７５℃以上开始析出的，并且在重新加热至固液两相区５７５－５９０℃内保温一段时间后，这种近球形α相仍然存在。
2) sphere like α phases
近球形的α相
3) sphere-shaped α-Fe_2O_3
球形α-Fe2O3
1.
Nano sphere-shaped α-Fe_2O_3 synthesized hydrothermally from pyrite slag;
5℃/min的条件下加热至(172±2)℃水热反应2h,得到粒度约为55nm的均匀球形α-Fe2O3。
4) morphology of primary α phase
α相形态
1.
The results show that,at 450℃ with different holding time from 3 h to 12 h,morphology of primary α phase is converted from irregular dendrite to granular homogeneous equiaxed grains then to rosette structure.
研究了热处理温度和保温时间对B细化Al-7Si合金的α相形态与硬度的影响,并确定了最佳热处理工艺。
6) pseudo-spherical α-Fe2O3
准球形α-Fe2O3
1.
A continuous uniform layer of amorphous TiO2 obtained by the hydrolysis of TBOT could be deposited on the surface of monodispersed pseudo-spherical α-Fe2O3.
钛酸四丁酯(TBOT)水解产生的TiO2沉积在单分散准球形α-Fe2O3颗粒的表面,形成均匀、连续的核-壳结构。
补充资料：α,α,α,α',α',α'-六氯对二甲苯
分子式：C8H4Cl6
分子量：312.84
CAS号：68-36-0
性质：白色针状或粉末状结晶。熔点108-110℃。溶于二甲苯、石油醚、乙醇、植物油，不溶于水。无味，有特殊臭味，遇光、碱会缓慢分解而呈酸性。
制备方法：以混二甲苯为原料，先用98%硫酸磺化，使间二甲苯生成间二甲苯磺酸盐。从磺化反应物中分离出含邻、对二甲苯的油层，水洗、干燥，减压蒸馏出邻、对二甲苯。间二甲苯磺酸盐经水解可得副产品间二甲苯。由邻、对二甲苯经氯化即得1，4-双（三氯甲基）苯：在反应锅中投入邻、对二甲苯，再加入过氧化苯甲酰和三乙醇胺。加热到70℃后，在光照射下导入氯气，于70-80℃反应6h，再升温至100-120℃继续反应，至反应液相对密度达到1.560-1.580（65℃），即为反应终点，停止通氯，减压脱除余氯。降温至5℃，过滤，洗涤得粗品，重结晶，活性炭脱色得成品。
用途：抗血吸虫病药物。对肝吸虫病、阿米巴原虫病、疟疾以及肠道线虫有一定疗效。但对神经系统的不良反应较多见，且延迟反应持续较久。
分子量：312.84
CAS号：68-36-0
性质：白色针状或粉末状结晶。熔点108-110℃。溶于二甲苯、石油醚、乙醇、植物油，不溶于水。无味，有特殊臭味，遇光、碱会缓慢分解而呈酸性。
制备方法：以混二甲苯为原料，先用98%硫酸磺化，使间二甲苯生成间二甲苯磺酸盐。从磺化反应物中分离出含邻、对二甲苯的油层，水洗、干燥，减压蒸馏出邻、对二甲苯。间二甲苯磺酸盐经水解可得副产品间二甲苯。由邻、对二甲苯经氯化即得1，4-双（三氯甲基）苯：在反应锅中投入邻、对二甲苯，再加入过氧化苯甲酰和三乙醇胺。加热到70℃后，在光照射下导入氯气，于70-80℃反应6h，再升温至100-120℃继续反应，至反应液相对密度达到1.560-1.580（65℃），即为反应终点，停止通氯，减压脱除余氯。降温至5℃，过滤，洗涤得粗品，重结晶，活性炭脱色得成品。
用途：抗血吸虫病药物。对肝吸虫病、阿米巴原虫病、疟疾以及肠道线虫有一定疗效。但对神经系统的不良反应较多见，且延迟反应持续较久。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条