1) Hydrothermal synthesis
水热法合成
1.
The title complex (C 32 H 30 Fe2N4O5) containing N, N′-Bis(Salicylideneamino) Ethanato Schiff base was prepared by hydrothermal synthesis and characterized by elemental analysis, IR, and single-crystal X-ray diffraction.
水热法合成得到一个含有水杨醛Schiff碱的双核铁配合物(C32H30Fe2N4O5),通过元素分析、红外光谱、X射线单晶衍射等手段对结构进行了表征。
2) hydrothermal synthesis method
水热合成法
1.
The good application prospects of calcium sulfate whisker(CSW) was reveiwed,and it was pointed out that hydrothermal synthesis method is the best preparation method on the basis of experiment,the key technology in preparation and application process is proposed,it include the number of H_2O in producation,oritating growth controlling,surface modification.
评述了硫酸钙晶须(CSW)作为增强组元的良好应用前景,并在实验研究的基础上指出水热合成法是目前最成功的CSW制备方法,提出CSW制备和应用过程中的关键技术:即产物结晶水的控制、定向生长控制技术、表面改性技术,并进行了相应评论。
3) hydrothermal method
水热合成法
1.
Study on the condition for preparation of magnesia-alumina spinel by hydrothermal method;
水热合成法制备镁铝尖晶石工艺条件研究
2.
Synthesis of SAPO-34 molecular sieve with hydrothermal method
水热合成法合成SAPO-34分子筛
3.
Zr-doped TiO2 nanotubes were successfully synthesized by a hydrothermal method, using Zr-doped anatase TiO2 powders as precursor.
采用水热合成法以锐钛型Zr/TiO2纳米粒子为原料制备了掺杂锆二氧化钛纳米管,用TEM、EDS、BET对其进行了表征。
4) hydrothermal synthesis
水热合成法
1.
Effects of Tweens and sodium dodecyl sulfate as modifiers on hydrothermal synthesis of nanocrystals copper;
吐温和十二烷基硫酸钠作修饰剂对水热合成法制备纳米铜的影响
2.
Preparation and photocatalytic activities of TiO_2 nanoparticles with sol-gel method and hydrothermal synthesis;
利用Sol-Gel法与水热合成法制备纳米TiO_2及其光催化活性研究
3.
The nanometer bismuth oxide powders are prepared by hydrothermal synthesis method with bismuth nitrate solutions as raw material,strong aqua ammonia or sodium hydroxide as mineralizer.
以Bi(NO3)3为原料,浓氨水或NaOH为矿化剂,采用水热合成法制备纳米Bi2O3粉体,并以XRD,TEM和IR进行表征,以样品对水中罗丹明B的光催化降解性能为评价指标,对样品的光催化性能进行了评价。
5) combustion synthesis-hydrothermal treatment
燃烧合成-水热法
1.
Preparation of bioceramic coating by combustion synthesis-hydrothermal treatment;
燃烧合成-水热法制备生物陶瓷涂层
6) stepwise hydrothermal synthesis assembled method
分步水热合成法
1.
By using stepwise hydrothermal synthesis assembled methods,magnetic materials Fe_3O_4 were successfully assembled into the pores of zeolites ZSM-5 for the first time,whose aperture is 0.
首次以分步水热合成法于孔径为 0 5 6nm的沸石分子筛ZSM 5的孔道中成功地组装了铁氧体Fe3 O4,并测出了它们的磁滞回线及磁学参数 :饱和磁化强度σs、剩余磁化强度σr 和矫顽力Hc 。
补充资料：晶体生长水热法
分子式：
CAS号：
性质： 在高温、高压水溶液中进行化学合成的一种方法。水热法不仅可以用于制备分子筛类的化合物，而且可以用来生长无机固体材料晶体。水的临界温度和压力分别为374℃和22MPa。在高温和高压下，水的离子积很大；例如在600℃和202.65MPa时，水的离子积是常温常压时的105倍。这意味着许多在通常条件下不溶于水的物质，在高温高压下可以溶于水。如果使体系产生一定的温度梯度，由于在不同温度下材料的溶解度不同，使材料晶体结晶出来。水热法生长晶体要在耐高压和高温的反应釜中进行。工业上应用水热法生长大尺寸的石英晶体。在生长晶体时，常在水中加入一定量的碱或酸，调节溶液的酸度，以调整材料在水中的溶解度。
CAS号：
性质： 在高温、高压水溶液中进行化学合成的一种方法。水热法不仅可以用于制备分子筛类的化合物，而且可以用来生长无机固体材料晶体。水的临界温度和压力分别为374℃和22MPa。在高温和高压下，水的离子积很大；例如在600℃和202.65MPa时，水的离子积是常温常压时的105倍。这意味着许多在通常条件下不溶于水的物质，在高温高压下可以溶于水。如果使体系产生一定的温度梯度，由于在不同温度下材料的溶解度不同，使材料晶体结晶出来。水热法生长晶体要在耐高压和高温的反应釜中进行。工业上应用水热法生长大尺寸的石英晶体。在生长晶体时，常在水中加入一定量的碱或酸，调节溶液的酸度，以调整材料在水中的溶解度。