1) forge aluminum alloy LD7
锻铝合金LD7
2) LD7 aluminum alloy
LD7铝合金
1.
Influence of thermo-deformation parameters on the flow stress of LD7 aluminum alloy;
热变形参数对LD7铝合金流动应力的影响
2.
The flow stress behavior of LD7 aluminum alloy, microstructure and .
在Gleeble-1500热模拟机上对LD7铝合金进行等温热变形实验,变形温度为300-500℃,应变速率为 0。
3.
Potentiodynamic polarization and electrochemical impedance spectroscopy(EIS) were used to study the influences of sealing methods on the corrosion behavior of anodic oxide film on LD7 aluminum alloy in NaCl solution.
研究了不同封闭方法对LD7铝合金阳极氧化膜在NaCl溶液中耐蚀性的影响,包括沸水封闭、氟化镍封闭、重铬酸钾封闭和醋酸镍封闭。
4) aluminium alloy forgings
铝合金锻件
1.
Ultrasonic examination about oxide film in aluminium alloy forgings;
铝合金锻件氧化膜缺陷超声波探伤
5) 2A14 aluminum alloy
2A14锻铝合金
1.
The surface roughness Ra value of 2A14 aluminum alloy is obtained by orthogonal experiment,and the principal and subordinate order of impact on Ra value of depth of cut,main shaft speed and amount of feed are studied with the method of variance analysis to get the optimal cutting parameters.
通过正交试验得到车削2A14锻铝合金时的表面粗糙度Ra值;利用方差分析的方法研究了切削深度、主轴转速和进给量三个独立因素对Ra值影响的主次顺序,并获得最佳的切削参数组合。
6) forging Al alloy
锻造铝合金
补充资料：耐热锻铝合金
分子式：
CAS号：
性质：一种耐热变形铝合金。通常采用铝铁镁铁镍合金。组织中主要的强化相是Al2CuMg和FeNiAl6。常用牌号有LD7，LD8和LD9。具有较好的耐热性，较小的热膨胀系数、良好的导热性和加工性能，可加工成各种铝材和锻件，用作在150～250℃工作的各种结构零件。
CAS号：
性质：一种耐热变形铝合金。通常采用铝铁镁铁镍合金。组织中主要的强化相是Al2CuMg和FeNiAl6。常用牌号有LD7，LD8和LD9。具有较好的耐热性，较小的热膨胀系数、良好的导热性和加工性能，可加工成各种铝材和锻件，用作在150～250℃工作的各种结构零件。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。