1) supper thin high speed cast mills
超薄快速铸轧机
2) ultra thin high speed roll casting
超薄快速铸轧
1.
Based on this fact,a virtual simulation of ultra thin high speed roll casting is carried out.
在此基础上 ,对超薄快速铸轧条件进行了虚拟仿真研究 ,研究结果表明 :不增强铸轧辊内、外冷却能力的条件下 ,而仅仅减薄铸轧板坯厚度即可提高铸轧速度 ;在其它工艺参数保持不变 ,且保持出口温度与常规铸轧时基本相近的出口温度时 ,铸轧厚度减薄时轧制压力比常规铸轧高 ;随着铸轧速度与铸轧区增大、铸轧坯厚度减薄、铸轧辊径增大 ,轧制压力峰值增大。
2.
The speed of ultra thin high speed roll casting is ten times,even more than twenty times as high as that of the conventional roll casting.
超薄快速铸轧速度可达常规铸轧速度的十几倍 ,甚至二十几倍 ,在快速铸轧条件下铸造区长度将增加 ,其轧制压力分布对总轧制力的影响就不可忽略。
3.
The temperature gradient is very great in the rolling zone under the ultra thin high speed roll casting condition,and the rolling pressure is strongly coupled function of the temperature.
超薄快速铸轧条件下轧制区内温度梯度很大 ,其轧制压力是温度的强耦合函数。
3) high-speed roll casting
快速铸轧
1.
ANSYS-based finite element simulation on temperature field of high-speed roll casting process;
基于ANSYS的快速铸轧过程温度场数值模拟
2.
The research of high-speed roll casting plastic deformation simulating are reached on the basis of the elastic-plastic deformation theory.
在弹塑性有限变形理论基础上,对快速铸轧塑性变形仿真建模进行了研究。
3.
The static equilibrium differential equation in casting and rolling zones during high-speed roll casting process is deduced respectively using the slab method.
在此基础上，对快速铸轧进行了虚拟仿真研究，研究结果表明：不增强铸轧辊内、外冷却能力，单纯减薄铸轧板坯厚度即可提高铸轧速度；随着铸轧速度降低与铸轧区增大以及铸轧坯厚度减薄，轧制压力峰值增大；随着铸轧辊径增大，轧制压力提高，因此铸轧机力能设计参数也要相应增大。
5) twin-roll continuous casting / the high speed thin gauge twin-roll casting
双辊连续铸轧/快速铸轧
6) high-speed twin roll cast-rolling
快速双辊铸轧
补充资料：渤海铝业有限公司铝板坯连铸连轧机生产卷毛料
渤海铝业有限公司铝板坯连铸连轧机生产卷毛料
渤海铝业有限公司铝板坯连铸连轧机生产卷毛制