1) W alloying
W合金化
1.
The experimental results show that the W alloying changes the cast structure and does not change the structure after heat process of high Nb TiAl alloy.
试验结果表明 ,W合金化能改变高铌TiAl合金的铸态组织 ,但不能改变热加工组织以及 4种典型组织和温度对其力学性能的影响。
2) Ni-W alloy
Ni-W合金
1.
Study on mechanical properties of Ni-W alloy films in micro-electro-mechanical system
MEMS中Ni-W合金薄膜力学性能的研究
2.
The Ni-W alloy plates were prepared by electro-deposition on copper substrate using nickel sulphate and sodium tungstate as precursors.
以硫酸镍及钨酸钠为主盐,采用电沉积法在Cu基体上制得了Ni-W合金镀层。
3.
Decorative Ni-W alloy deposits alternative to chromium was prepared by electroplating in citric acid solution.
在柠檬酸溶液体系中,通过电沉积制备出了Ni-W合金装饰性代铬镀层。
3) W-Cu alloy
W-Cu合金
1.
Effect of Cu content on rapid sintering W-Cu alloy under the action of electric field;
Cu含量对电场快速烧结W-Cu合金的影响
2.
Effect of metal elements on rapid sintering W-Cu alloy under the action of electric field;
电场作用下金属元素对W-Cu合金快速烧结的影响
3.
High copper W-Cu alloy can be obtained by infiltration of tungsten and copper powder.
通过选择不同粒度的原料钨粉,采用预混合部分铜粉然后渗铜的方法制备一系列不同铜含量的W-Cu合金。
4) W-15Cu alloy
W-15Cu合金
1.
Study on control of pores in W-skeleton in preparing W-15Cu alloy;
W-15Cu合金制备中钨骨架孔隙控制的研究
5) W/Cu alloy
W/Cu合金
6) Ni–W alloy
Ni–W合金
补充资料：表面合金化
| 表面合金化 surface alloying 通过扩散改变基体金属表面层的成分和组织的材料保护技术。机械制造中常用的是铝、铬、硅、钒和锌等的表面合金化层或渗层（利用金属卤化物蒸气与金属表面层产生化学反应或在液相中发生化学反应而形成）。①铝渗层，可用作碳素钢或低合金钢等制成的空气加热器、加热炉和蒸气过热器构件的覆层，层厚约125～1000微米，含铝约25％。②铬渗层，可用粉末法或熔盐法在低碳钢、高碳钢、合金钢、不锈钢、工具钢、铸铁和铁粉烧结件上生成，其抗蚀性相当于含铬30％的钢。碳铬层的硬度很高，耐磨性好，多用于保护阀门、喷嘴、泵、量规和工模具。③硅渗层，具有耐磨、耐蚀性能，硬度高，还具有良好的抗擦伤性，主要用于低碳(含碳小于0.25％)、低硫(含硫小于0.04％)钢等制成的泵轴、缸衬、阀门、传送带链的联结件和洗瓶机的构件等。④钒渗层 ，基体钢材中的碳含量至少应为0.4％，该渗层的硬度很高，但冷焊性不佳。⑤锌渗层，主要用在铁基体材料上，该渗层的特点是厚度均匀，抗腐蚀性能好。 |