1) deformation microstructure
形变显微组织
1.
Tensile deformation microstructure of aluminum single crystal was characterized by TEM and EBSD techniques.
结果发现 ,单晶铝形变显微组织中表现为明显的带状特征 ,TEM及EBSD技术的表征结果非常吻合 ,但EBSD不能完全反映出位错界面的分割特征 ;相对于TEM而言 ,EBSD技术所能分析的试样区域较大 ,其结果具有较好的统计意
2.
It is found that different types of deformation microstructures develop depending on the grain orientation.
结果发现 :多晶铜的形变显微组织表现为 3种不同类型 ,形变显微组织与晶粒的晶体学取向存在明显的依赖关系 ;在对不同形变显微组织中位错边界两侧亚晶的取向差及位错边界间距进行定量分析的基础上 ,估算了每一类型组织的位错密度及其储存能 ,发现不同类型组织间存在明显的差别 ;对形变后的试样进行再结晶退火后发现 ,再结晶形核机制为晶界弓出形核 ,晶界弓出方向为储存能较高的晶粒。
2) Microstructure Evolution
显微组织演变
1.
Effect of electrolytic copper powder and atomizing copper powder to microstructure evolution during SPS;
电解铜粉和雾化铜粉对SPS过程中显微组织演变的影响
3) Microstructural evolution
显微组织演变
1.
In order to investigate the microstructural evolution of Ni3Al intermetallic from Al and Ni powders during self-propagating high-temperature synthesis (SHS), a combustion front quenching method (CFQM) was used for extinguishing the propagating combustion wave.
为了研究用Ni粉和Al粉自蔓延高温合成(SHS)Ni3Al过程中的显微组织演变,用燃烧波淬熄法使蔓延的燃烧波自行熄灭,用扫描电子显微镜(SEM)及能谱仪(EDS)观察和分析了淬熄试样中的显微组织,测试了燃烧温度,并用X射线衍射(XRD)分析了合成产物的相组成。
2.
The microstructural evolution pattern of Al/Mg2Si composite during self-propagating high-temperature synthesis(SHS) was studied by means of combustion front quenching.
采用燃烧波前沿淬熄法研究Al/Mg2Si复合材料在自蔓延高温合成(SHS)过程中的显微组织演变规律。
4) microscopic structure
显微组织
1.
The influence of rotating magnetic field on the microscopic structure of welded metal by laser welding;
旋转磁场对激光焊缝金属显微组织的影响
2.
The microscopic structure of the plane-spring made of 60si2Mn steel after the fatigue crack is observed and analyzed with mettaloscope.
通过金相显微镜对60Si2Mn钢制汽车板簧疲劳损坏的过程进行显微组织分析,研究了疲劳裂纹萌生的位置、扩展过程和扩展途径,探索提高汽车板簧疲劳寿命的有效方法。
3.
The results show that the joint with good microscopic structure and mechanical property can be obtained by using optimized welding process parameters and rational heat treating process after welding.
对 45钢 /W8Co3N高速钢刀具的摩擦焊接工艺及焊接效果进行了试验研究 ,结果表明 ,采用优化的摩擦焊接工艺参数及合理的焊后热处理工艺可获得具有良好显微组织和力学性能的焊接接头。
5) micro-structure
显微组织
1.
With the help of metal graphic microscope,micro-structure of different section of weld.
借助金相显微镜,观察分析了不同冷却速度下的显微组织和焊接接头不同部位的显微组织。
2.
, the chemical composition, manufacturing process, micro-structure, strenthening mechanism, properties, applications, grades and specifications.
全面地描述了非调质钢的发展概况，分析了非调质钢发展过程中化学成分、加工工艺、显微组织、强化机制、性能、应用范围、品种规格等方面特征的变化。
6) microstructures
显微组织
1.
Effect of pre-annealing on microstructures and soft magnetic properties of nanocrystalline Fe_(86)Zr_7B_6Cu_1 alloy;
预退火对纳米晶Fe_(86)Zr_7B_6Cu_1合金显微组织和软磁性能的影响
2.
Effects of La on Microstructures of Industrial Pure Aluminum;
镧对工业纯铝显微组织的影响
3.
Effects of trace element Ag on microstructures and mechanical properties of Al-8Cu-0.5Mg alloy;
微量Ag对Al-Cu-Mg合金显微组织与力学性能的影响