1) YSZ
钇稳定化氧化锆
1.
Study on the Properties of YSZ Electrolyte Fabricatedby Plaster Casting Method;
注浆成型法制备的钇稳定化氧化锆电解质性能研究
2.
The yttria stabilized zirconia (YSZ) porous ceramic tubes with a porosity of 49 0%~64 1% were fabricated by slip casting method with YSZ powder as the aggregate, arabic gum as the dispersant and the binder, and optimized corn meal as the pore forming agent.
以钇稳定化氧化锆 (YSZ)为骨料 ,优选出玉米粉为成孔剂 ,阿拉伯树胶为分散剂和粘结剂 ,采用注浆法制备出孔隙率为 49。
3.
The stability of suspension made of 8% yttria stabilized zirconia (YSZ) micro size powder with 4% Al 2O 3 added and arabic gum as the dispersant was studied.
研究摩尔分数为 8%的钇稳定化氧化锆 ( YSZ)微粉添加质量分数为 4%的 Al2 O3 ,并以阿拉伯树胶为分散剂所制备的料浆的稳定性 。
2) Yttrium stabilized zirconia(YSZ)
钇稳定氧化锆(YSZ)
4) yttria-stabilized zirconia
钇稳定氧化锆
1.
Yttria-stabilized zirconia (YSZ) is widely used as the solid electrolyte in solid oxide fuel cell (SOFC) because of its high oxygen conductivity and good chemical stability under the condition of the application.
钇稳定氧化锆(YSZ)具有氧离子电导率高及在工作环境下化学稳定性好等特点，在固体氧化物燃料电池(SOFC)中得到广泛应用。
5) yttria-stabilized zirconia balls
钇稳定氧化锆球
6) yttria stabilized zirconia(8YSZ)
钇全稳定氧化锆
1.
The sintering process of 8%(mole fraction,the same below) yttria stabilized zirconia(8YSZ) nano powders was investigated.
实验研究了钇全稳定氧化锆(8YSZ)纳米粉体的烧结工艺,根据阿基米德原理测瓷体密度,通过测定烧结前后瓷片尺寸获得烧结线收缩率,使用扫描电子显微镜观测样品微观形貌,并探讨了纳米粉体烧结的致密化过程,分析了烧结工艺对致密度和晶粒大小的影响,得到了8YSZ纳米粉体合理的烧结工艺为:采用两步烧结,首先升温到1500℃,升温速率为3℃/min,然后降低温度到1450℃,烧结时间为4h。
补充资料：氧化锆-氧化钇红外陶瓷
分子式： ZrO2-Y2O3
CAS号：
性质：一种以二氧化锆为基体固溶6％～8％(mol)氧化钇的红外光学材料。立方晶结构。熔点2700℃。密度5.98g/cm3。红外透射波段1～10μm。采用1450℃以上高温烧结或1300～1700℃，50～300MPa热压制取。用于制造耐高温红外窗口和整流罩。
CAS号：
性质：一种以二氧化锆为基体固溶6％～8％(mol)氧化钇的红外光学材料。立方晶结构。熔点2700℃。密度5.98g/cm3。红外透射波段1～10μm。采用1450℃以上高温烧结或1300～1700℃，50～300MPa热压制取。用于制造耐高温红外窗口和整流罩。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条