1) HDPE/PET/EVA blends
HDPE/PET/EVA共混体系
2) PET Blends
PET共混体系
1.
Study on Structures and Properties of PET Blends and GF/PET Composites in Shear Field;
剪切场中PET共混体系及玻纤增强体系结构与性能的研究
3) HDPE/PC blends
HDPE/PC共混体系
1.
HDPE and PC are known to be incompatible polymer pair, therefore how to compatibilize and improve the properties of HDPE/PC blends have become the important problem.
本文通过双螺杆反应挤出熔融加工过程,促使乙烯-醋酸乙烯酯共聚物(EVA)、乙烯-丙烯酸共聚物(EAA)侧基上的官能团与PC组分主链上的酯基在催化剂氧化二丁基锡(DBTO)的作用下发生酯交换或酸-酯交换反应,在共混体系界面原位生成接枝或共交联的PC-EVA、PC-EAA共聚物,作为HDPE/PC共混体系的增容剂,从而达到原位增加HDPE/PC共混体系相容性的目的。
4) PVC/EVA blends
PVC/EVA共混体系
5) PET/PC blends
PET/PC共混体系
1.
The crystallized samples of 20%PC in PET/PC blends mixed at 30 r/min and 523, 533 and 553 K for 15 min were obtained at 300 MPa and 613 K for 6 h with a self-made piston-cylinder high-pressure apparatus.
利用转矩流变仪、DSC、SEM及WAXD等表征手段研究了PET/PC共混体系的酯交换反应对其高压结晶行为的影响。
6) PA 6/PET blend
PA 6/PET共混体系
补充资料：PC/PET blend PC/PET
分子式：
CAS号：
性质： 共混物一般采用机械共混法制备，具有较好的相容性，尤其当PET/PC在60％～70％/40％～30％的共混比例下相容性最好，若PET含量少于上述比例，则共混物具有两相结构。其特点是：有较优良的拉伸强度和加工流动性，在宽广的温度范围内有很高的冲击强度，悬臂梁冲击强度在室温时为960J/m，在-20℃时仍保持为693J/m。有优异的耐化学腐蚀性，司在汽油、机油中工作，并且无应力开裂。刚性好，耐磨，尺寸稳定。耐热性好，加工工艺性良好等。该类共混物适于制造汽车零件，运动器材，草地及园艺工具，各种工业用机械零件。用此类共混物代替超韧尼龙在高温、低温和化学腐蚀性强的环境中使用，能保持良好的尺寸稳定性。
CAS号：
性质： 共混物一般采用机械共混法制备，具有较好的相容性，尤其当PET/PC在60％～70％/40％～30％的共混比例下相容性最好，若PET含量少于上述比例，则共混物具有两相结构。其特点是：有较优良的拉伸强度和加工流动性，在宽广的温度范围内有很高的冲击强度，悬臂梁冲击强度在室温时为960J/m，在-20℃时仍保持为693J/m。有优异的耐化学腐蚀性，司在汽油、机油中工作，并且无应力开裂。刚性好，耐磨，尺寸稳定。耐热性好，加工工艺性良好等。该类共混物适于制造汽车零件，运动器材，草地及园艺工具，各种工业用机械零件。用此类共混物代替超韧尼龙在高温、低温和化学腐蚀性强的环境中使用，能保持良好的尺寸稳定性。