2) MCM-41 mesoporous materials
MCM-41介孔材料
1.
Using cetyl-trimethyl-ammonium bromide (CTMAB) as template and tetraethylortho-silicate (TEOS) as silica source, the MCM-41 mesoporous materials incorporated in framework by Y, Nd and Sm were synthesized by hydrothermal synthesis method.
以十六烷基三甲基溴化铵(CTMAB)为模板剂,以正硅酸乙酯(TEOS)为硅源,采用水热晶化法成功合成了Y,Nd,Sm骨架负载的MCM-41介孔材料,通过XRD,N2吸附脱附、SEM,IR,TG-DTA等测试手段对其孔结构、微形貌和Y,Nd,Sm的存在状态进行了表征。
3) MCM-41 ordered mesoporous materials
MCM-41有序介孔材料
4) mesoporous MCM-41
介孔MCM-41
1.
Preparation and properties for epoxy resin/nano-sized mesoporous MCM-41 composite by supercritical CO_2;
超临界CO_2方法制备环氧树脂/纳米介孔MCM-41复合材料
2.
Effect of silane coupling agent modified MCM-41 on theproperties of epoxy resin/nanosized mesoporous MCM-41 composites;
硅烷修饰对环氧树脂/纳米介孔MCM-41复合材料性能的影响
3.
The influences of the different shape and the different size of nano-sized mesoporous MCM-41 on the tensile properties and thermo-stability were investigated.
用熔融共混法制备出聚丙烯基纳米复合材料,研究了形状和大小不同的纳米介孔MCM-41填充物对聚丙烯基纳米复合材料的拉伸性能与热性能的影响。
5) MCM-41 mesoporous sieve
MCM-41介孔分子筛
1.
Recent advance on the modification of MCM-41 mesoporous sieve by incorporation,function and support were reviewed,and its application in chemical engineering,environmental protection and biological medicine were summarized.
综述了近年来通过搀杂、有机官能化、负载的方法改性MCM-41介孔分子筛的研究情况,重点介绍了MCM-41介孔分子筛在化工、环保、生物医学领域的应用现状。
6) MCM-41 mesoporous molecular sieve
MCM-41介孔分子筛
1.
The silica MCM-41 mesoporous molecular sieve has some advantages,for instance,stable framework,ordered pore canal,narrow distrbution of pore diameter,but its hydrothemal stability is terrible,acidity is inferior,pore diameter is not big enough and it isn't suitable for large molecule reaction.
纯MCM-41介孔分子筛具有稳定的骨架结构、孔道规则排列有序、孔径分布窄等优点,但其水热稳定性较差、酸性弱、孔径不够大、难以用于大分子反应。
2.
β-Tetra-(p-carboxyphenoxy)phthalocyanine cobalt((p-HOOCPhO)4PcCo)was loaded on MCM-41 mesoporous molecular sieves by impregnation to prepare(p-HOOCPhO)4PcCo/MCM-41 catalyst which was used in oxidation of ethanethiol.
采用浸渍法将β-四(4-羧基苯氧基)酞菁钴((p-HOOCPhO)4PcCo)负载在MCM-41介孔分子筛中制备了(p-HOOCPhO)4PcCo/MCM-41催化剂,通过X射线衍射、紫外-可见漫反射光谱、Raman光谱、N2吸附方法对催化剂的结构和组成进行了表征,研究了常温、常压下,该催化剂催化氧化乙硫醇反应的动力学。
补充资料：机械工程材料:粉末冶金多孔材料
用粉末冶金的方法製造的﹑内部结构为多孔的材料(或製品)﹐一般由球状或不规则形状的金属或合金粉末经成形和烧结製成﹐又称烧结多孔材料。这种材料为孔道纵横交错﹑互相贯通的多孔体﹐通常具有30～60％体积的孔隙度﹐孔径1～100微米。常用的金属或合金有青铜﹑不锈钢﹑铁﹑镍﹑鈦﹑钨﹑鉬以及难熔金属化合物等。做成的製品有坩堝状﹑碟状﹑管状﹑板状﹑薄膜等。粉末冶金多孔材料的特点是﹕孔径和孔隙度均可控制﹔优良的透过性能﹐且在使用后可以再生﹐因而使用寿命长﹔导热﹑导电﹔耐高温﹑耐低温﹑抗热震﹔抗介质腐蚀﹔比表面积大﹔可焊接和加工等。因此它的综合性能较传统的纸质﹑棉和化纤织品﹑陶瓷﹑玻璃﹑金属丝网等过滤材料为好。在现代技术中﹐多孔材料愈益发挥其重要作用﹐有两方面的主要用途。作过滤器用﹕利用其多孔的过滤分离作用净化液体和气体。例如用来净化飞机和汽车上的燃料油和空气﹔化学工业上各种液体和气体的过滤﹔原子能工业上排出气体中放射性微粒的过滤等。利用其孔隙的作用﹐製造多孔电极﹑灭火装置﹑防冻装置﹑耐高温喷嘴等。多孔电极主要在电化学方面应用。灭火装置是利用其抗流作用而防止爆炸﹐如气焊用的火焰防爆器等。防冻装置是利用其多孔可通入预热空气或特殊液体﹐用来防止机翼和尾翼结冰。耐高温喷嘴则是利用表面发汗而使热表面冷却的原理﹐被称为发汗材料。(见彩图 粉末冶金多孔材料 )