1) high C-Cr cast steel
高碳铬铸钢
1.
Results show that RE and heat, treatment improves the morphology and the distribution of carbide and increases the impact toughness of high C-Cr cast steel.
研究了稀土与热处理对高碳铬铸钢碳化物的形态及冲击韧性的影响。
3) high chromium cast steel
高铬铸钢
1.
The laser melting was performed on high chromium cast steel nozzle of power boiler burner.
对电站锅炉燃烧器喷嘴用高铬铸钢材料进行了激光熔凝处理,研究了激光熔凝处理后高铬铸钢表面熔凝层的显微组织、相结构、维氏硬度及耐磨性能。
2.
This paper deals with the granular carbides formation from hot deformation in high chromium cast steel.
本文探讨了热变形高铬铸钢中颗粒状碳化物的形成。
4) High C Cr Steel
高碳铬钢
5) high carbide high chromium steel
高碳高铬钢
1.
The chemical compositions of high carbide high chromium steel and chromium-bearing grey cast iron were optimized through orthogonally designed experiments which were carried out on a horizontal cantilevered centrifugal machine to compound the steel and cast iron by way of a centrifugal casting process.
通过正交设计实验优化得到了高碳高铬钢、含铬灰铸铁的最优成分;采用卧式悬臂离心实验机对高碳高铬钢/含铬灰铸铁进行离心复合·在复合成功的基础上,利用金相显微镜对不同实验条件下的复合界面进行了对比、分析·结果表明:经离心复合铸造,高碳高铬钢/含铬灰铸铁复合界面为结合紧密的复合层;复合试样经1080℃保温1h,水淬+500℃回火1h处理后,复合界面碳化物扩散更充分,但对复合界面宽度没有影响;浇注温度提高,复合界面宽度增加,当高碳高铬钢液浇注温度由1460℃提高到1480℃时,复合界面宽度增加了100μm
6) high Cr-Ni cast steel
高铬镍铸钢
补充资料：三[2-[(9-十八碳烯酰基)氨基]苯甲酸O1,O2]铬
CAS：94232-92-5
中文名称：三[2-[(9-十八碳烯酰基)氨基]苯甲酸O1,O2]铬
英文名称：tris[2-[(1-oxo-9-octadecenyl)amino]benzoato-O1,O2]-Chromium；Chromium,tris[2-[(1-oxo-9-octadecenyl)amino]benzoato-O1,O2]-
中文名称：三[2-[(9-十八碳烯酰基)氨基]苯甲酸O1,O2]铬
英文名称：tris[2-[(1-oxo-9-octadecenyl)amino]benzoato-O1,O2]-Chromium；Chromium,tris[2-[(1-oxo-9-octadecenyl)amino]benzoato-O1,O2]-
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条