1) low carbon and high chromium cast iron
低碳高铬铸铁
1.
Based on sliding and drum wear test and microstucture examination,the influence of quenching temperature and holding time on wear resistance of low carbon and high chromium cast iron was inuvestigated.
通过滑动和滚筒式磨损试验及金相组织观察,研究了淬火温度及保温时间对低碳高铬铸铁耐磨性能的影响。
2) low carbon-high chromium cast iron
低碳高铬白口铸铁
1.
Effects of heat treatment on properties of low carbon-high chromium cast iron;
热处理对低碳高铬白口铸铁性能的影响
3) high chromium cast iron
高碳高铬铸铁
1.
Microstructures of high chromium cast iron for surfacing;
高碳高铬铸铁堆焊合金组织分析
5) low Mo-containing high chromium cast irons
低钼高铬铸铁
6) low-Cr cast iron
低铬铸铁
1.
The WC and low-Cr cast iron composite layer samples were prepared by casting-penetrating process to improve the wear resistance of the low-Cr cast iron.
为进一步提高低铬铸铁的耐磨性,利用铸渗工艺采用膏块法制备了WC/低铬铸铁复合铸渗层试样。
2.
VS+Ti+Zn compound inoculant plays a favorable role in improving property process of low-Cr cast iron.
在低铬铸铁改性处理中,VS+Ti+Zn复合孕育剂起着良好的孕育处理作用。
补充资料：高铬铸铁
分子式：
CAS号：
性质： 铬含量高的耐蚀耐热白口铸铁。依铬含量的不同，可分为铬含量26％～30％和32％～36％两类铸铁。在1000℃以上的氧化性气氛中，高铬耐热铸铁仍有好的抗氧化能力。有良好的强度以及较好的机械加工性能，但韧性较低，不宜用于温度急变场合。常用来制作加热炉炉底板、炉子传送链的构件等。
CAS号：
性质： 铬含量高的耐蚀耐热白口铸铁。依铬含量的不同，可分为铬含量26％～30％和32％～36％两类铸铁。在1000℃以上的氧化性气氛中，高铬耐热铸铁仍有好的抗氧化能力。有良好的强度以及较好的机械加工性能，但韧性较低，不宜用于温度急变场合。常用来制作加热炉炉底板、炉子传送链的构件等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。