1) La-Ti
镧钛
1.
Research on preparation of bentonite absorbent modified by La or La-Ti and its phosphor removal efficiency;
镧钛改性膨润土吸附剂的制备与除磷性能的研究
2) sodium lanthanum titanate
钛酸镧钠
3) bismuth lanthanum titanate
钛酸镧铋
4) loparite
['lɔpə,rait]
钠镧钛矿
1.
The structure of loparite with general formula Na_(1/2)Ln_(1/2)TiO_3 depends mainly on the elements at the Ln site.
钙钛矿 锶钛矿 钠镧钛矿三元系是钙钛矿族矿物的典型代表。
2.
The structure of loparite with general formula Na1/2Ln1/2TiO3 depends mainly on the elements at the Ln site.
钙钛矿—锶钛矿—钠镧钛矿三元系是钙钛矿族矿物的典型代表。
5) Titanlanthanate
钛镧酸盐
1.
Mild Hydrothermal Syntheses and Characterization of Nanocrystalline Titanlanthanates;
纳米晶钛镧酸盐的水热合成和表征
6) PLT
镧钛酸铅
1.
The results show that the crystalline temperature of PLT gel is about 500℃,the size of the powders is about 30nm when heated temperatures at 650℃ for 2h.
采用溶胶－凝胶法制备掺镧钛酸铅（ＰＬＴ）纳米晶，分别用Ｘ射线衍射仪、透射电子显微镜、红外光谱仪和差热扫描量热分析仪对其晶化温度、结构、形貌特性进行了分析测试。
补充资料：镁镧钛系陶瓷
分子式：MgO-La2O3-TiO2
CAS号：
性质：在MgO-La2O3-TiO2三元体系中主晶相为偏钛酸镁MgTiO3和二钛镧La2O3·TiO2的陶瓷材料。为调整瓷料介电常数温度系数常加入钛酸钙和金红石，形成二类瓷料体系：MgTiO3- La2O3·2TiO2- TiO2系和MgTiO3- La2O3·2TiO2- CaTiO3系。具有较高介电常数、较低介质损耗角正切值、高温（150℃）下介电性能良好。采用一般电子陶瓷工艺制造。用于制造高频温度补偿及热稳定电容器。
CAS号：
性质：在MgO-La2O3-TiO2三元体系中主晶相为偏钛酸镁MgTiO3和二钛镧La2O3·TiO2的陶瓷材料。为调整瓷料介电常数温度系数常加入钛酸钙和金红石，形成二类瓷料体系：MgTiO3- La2O3·2TiO2- TiO2系和MgTiO3- La2O3·2TiO2- CaTiO3系。具有较高介电常数、较低介质损耗角正切值、高温（150℃）下介电性能良好。采用一般电子陶瓷工艺制造。用于制造高频温度补偿及热稳定电容器。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。