1) anti-aging system
耐老化体系
1.
Used in thin LDPE/LLDPE and mLLDPE/LDPE green house films, 6911/B215 anti-aging system exhibits excellent anti-light, thermal-oxidation properties.
6911/B215耐老化体系应用于薄型LDPE/LLDPE棚膜和mLLDPE/LDPE棚膜表现出良好的耐光、热氧化效能,有效地解决了“背板效应”导致骨架处棚膜加速老化破裂的实际问题。
2) anti-ageing
耐老化
1.
Development of anti-ageing ABS/PVC;
耐老化ABS/PVC共混塑料的研制
2.
An anti-ageing ABS/PVC blend composite was prepared by adding antioxidants, ultraviolet absorbersin ABS/PVC basic formula and the effect of different ultraviolet absorbers, antioxidants on anti-ageingproperty of ABS/PVC blend composite was also studied.
在ABS/PVC基础配方中通过添加紫外线吸收剂、抗氧剂等助剂,研制了耐老化ABS/PVC共混塑料,并研究了不同品种的紫外线吸收剂和抗氧剂对提高ABS/PVC共混复合材料耐老化性能的影响。
3) aging resistance
耐老化
1.
Aging resistance asphalt was developed by research on ductility and penetration ratio of different crude oil and processing technology.
通过不同油种、不同组合工艺的沥青产品TFOT后15℃延度与沥青针入度之比及 钟入度比的考察,对沥青原料的油种进行选择,对加工工艺进行优化,研制开发了针入度比大 于70％、TFOT后15℃延度大于100 cm的耐老化型高等级道路用AH-70沥青产品。
2.
The results showed that by adding the FL, the flowability of the mixed NBR was increased, the mechanical properties of the NBR rubber bonded magnet markedly enhanced, and its aging resistance improved.
结果表明加入FL后提高了混炼胶的流动性,体系综合力学性能显著提高,硫化橡胶磁体的耐老化性也得到改善。
4) resistance to weathering
耐候老化
5) Aging Resistance
耐老化性
1.
Formula of chlorosulfonated polyethylene water resistance and aging resistance;
氯磺化聚乙烯的耐水性和耐老化性配方
2.
The water resistance and aging resistance of chloroprene vulcanizate were studied and a practical formula was obtained by the optimum ingredients choice.
为提高通用型氯丁橡胶硫化胶的耐水性和耐老化性，通过对配方中组分的优化选择，获得了实用性配方（质量份）：通用型氯丁橡胶／氯磺化聚乙烯８０／２０，硫化剂ＺｎＯ与ＰｂＯ（或Ｐｂ３Ｏ４）２０，促进剂ＮＡ─２２和促进剂ＴＴ（或ＤＭ）１～２，防老剂４０１０ＮＡ与防老剂ＡＷ（或Ａ，Ｄ）２。
3.
The mechanical performance,apparent density,thermal stability and aging resistance for prepared RPUF were separately tested.
在试验中,碱木质素按不同比例(5%～40%)代替聚醚多元醇与多亚甲基多苯基多异氰酸酯(PAPI)合成了RPUF,并系统分析了木质素的添加对合成的RPUF力学性能、表观密度、热学性能、耐老化性的影响。
6) anti-aging
耐老化
1.
Good application effect of 6911/B215 anti-aging system in thin mLLDPE film is presented.
阐明了解决mLLDPE熔体粘度大、熔体强度低、熔体易破裂等关键问题的工艺技术要点 ,介绍了高效 6 911/B2 15耐老化体系在薄型mLLDPE棚膜中的良好应用效果 ,报导了外涂型流滴消雾剂应用情况并提出了发展建议。
2.
This article introduced the basic properties and constitute material of plasticizers DR,confirmed the physic-chemical analysis of Yanggu Huatai\' plasticizer DR,by changing the plasticizer content,researched the effects on performance with the vulcanized rubber and non-vulcanized rubber,and verified the impact on vulcanized rubber with wear,anti-aging,processing and curing properties.
本文介绍了增塑剂DR的基本性能及构成材料,确认了阳谷华泰的增塑剂DR的物化分析结果,通过改变增塑剂含量,研究了增塑剂对未硫化橡胶和已硫化橡胶性能的影响,从而验证增塑剂高低对轮胎硫化橡胶耐磨、耐老化、加工性、延迟硫化等性能的影响,对轮胎企业橡胶配方设计有着重要的参考价值。
补充资料：耐人工加速老化性
分子式：
CAS号：
性质：是基于大量的天然曝露试验的结果，在实验室内人为地模拟气候的种种破坏因素，并给予一定的强化，以克服天然曝露试验需时过长的不足。强化包括光源（日光以紫外线灯代替，紫外线区的光线对材料的破坏性最大），温度（温度升高也促使漆膜加速老化），湿度（使紫外线照射的破坏作用增强），氧气（氧化作用促进老化引起的漆膜龟裂、漆膜失光）等方面。强化包括以紫外线光代替日光；以高温高湿代替常温常湿，以氧气代替空气，这些都可加速对漆膜的破坏，在短期内得到结果，但人工加速老化试验往往与天然曝晒试验的结果不完全一致，但在没有更好的办法之前，这仍不失为研究涂膜耐老化性能的一个捷径。
CAS号：
性质：是基于大量的天然曝露试验的结果，在实验室内人为地模拟气候的种种破坏因素，并给予一定的强化，以克服天然曝露试验需时过长的不足。强化包括光源（日光以紫外线灯代替，紫外线区的光线对材料的破坏性最大），温度（温度升高也促使漆膜加速老化），湿度（使紫外线照射的破坏作用增强），氧气（氧化作用促进老化引起的漆膜龟裂、漆膜失光）等方面。强化包括以紫外线光代替日光；以高温高湿代替常温常湿，以氧气代替空气，这些都可加速对漆膜的破坏，在短期内得到结果，但人工加速老化试验往往与天然曝晒试验的结果不完全一致，但在没有更好的办法之前，这仍不失为研究涂膜耐老化性能的一个捷径。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条