1) Corundum composite brick
刚玉复合砖
2) composite brown corundum brick
复合棕刚玉砖
1.
Research on the erosion mechanism of composite brown corundum bricks used for blast furnace hearth;
炉缸复合棕刚玉砖蚀损机理的探讨
3) β-SiAlON bonded corundum brick
β-SiAlON结合刚玉砖
1.
High temperature mechanical properties and microstructure of β-SiAlON bonded corundum bricks;
β-SiAlON结合刚玉砖的高温力学性能与显微结构
4) SiAlON-bonded corundum brick
SiAlON结合刚玉砖
1.
Multiple erosion of alkali metals and zinc to SiAlON-bonded corundum bricks for blast furnace;
碱金属和锌对高炉用SiAlON结合刚玉砖的复合侵蚀
5) Rebonded corundum brick
再结合刚玉砖
1.
Rebonded corundum brick made from sintered corundum;
用烧结刚玉研制再结合刚玉砖
6) Sialon bonded corundum bricks
赛隆结合刚玉砖
1.
Sialon bonded corundum bricks are produced using silicon, alumina and brown fused corundum as main starting materials in a flowing nitrogen atmosphere.
以工业硅粉、氧化铝和棕刚玉为主要原料 ,在氮化炉内烧成 ,生产了赛隆结合刚玉砖 ,其指标和性能达到和超过法国某公司同类产品 ,满足了武钢 1号高炉使用要
补充资料：轻质刚玉砖
分子式：
CAS号：
性质：又称为氧化铝隔热砖（aluminium oxide heat insulating brick），泡沫刚玉砖或泡沫氧化铝砖（foamed aluminium oxide brick）。含氧化铝在90%以上（foamed corundum brick）、主要由刚玉组成的轻质耐火材料。耐火度较高，重烧体积收缩率小。耐压强度4～25MPa，体积密度为0.8～1.35g/cm3。导热性低。抗热震性能好。通常以工业氧化铝为原料，加少量软质黏土及结合剂，共同磨成泥浆，采用泡沫法或气体发生法，经浇注成型、干燥，在1400～1550℃烧成。可用于热工设备的隔热层，或与火焰直接作用的热工设备内衬，但不宜用于受熔渣直接浸蚀处。在还原气氛下使用也有较高的稳定性。最高使用温度一般可达1650℃，纯度高的制品可达1800℃。
CAS号：
性质：又称为氧化铝隔热砖（aluminium oxide heat insulating brick），泡沫刚玉砖或泡沫氧化铝砖（foamed aluminium oxide brick）。含氧化铝在90%以上（foamed corundum brick）、主要由刚玉组成的轻质耐火材料。耐火度较高，重烧体积收缩率小。耐压强度4～25MPa，体积密度为0.8～1.35g/cm3。导热性低。抗热震性能好。通常以工业氧化铝为原料，加少量软质黏土及结合剂，共同磨成泥浆，采用泡沫法或气体发生法，经浇注成型、干燥，在1400～1550℃烧成。可用于热工设备的隔热层，或与火焰直接作用的热工设备内衬，但不宜用于受熔渣直接浸蚀处。在还原气氛下使用也有较高的稳定性。最高使用温度一般可达1650℃，纯度高的制品可达1800℃。