1) waste magnesia brick
废镁砖
1.
Pilot study on magnesium removal using sulphric acid from copper-smelting furnace lining waste magnesia brick;
铜冶炼炉炉衬废镁砖硫酸脱镁试验研究
2.
To increase recovery of high carbon ferrochrome, the effecting factors of chrome contents in slags were analysed, and the preliminary test of adding waste magnesia brick and magnesite were conducted.
为了提高高碳铬铁的回收率,分析了影响渣中铬含量的因素,并通过配加废镁砖和菱镁矿作了初步试验。
4) crushed brick
废砖
1.
As one of the main components of construction waste,the degree and way of resource utilization of crushed brick directly affects the process of resource recovery and industrialization of construction waste.
废砖是建筑垃圾主要组成成分之一,其资源化利用程度和途径直接影响建筑垃圾资源化、产业化进程。
5) magnesite brick
镁砖，苦土砖
6) Magnesia-chrome brick
镁铬砖
1.
Destruction mechanism of magnesia-chrome bricks for different kinds of high-temperature furnace
不同类型高温窑炉用镁铬砖损毁机理分析
2.
This paper describes the influence of production condition of the dry-process cement rotary kiln on the service life of the magnesia-chrome brick.
为了实现我国大型干法水泥回转窑烧成带用直接结合镁铬砖的国产化,本文分析了干法水泥生产工艺条件对镁铬砖使用寿命的影响,总结了国外对镁铬砖损毁机理的研究结果,优化了水泥窑用直接结合镁铬砖的原料及生产工艺,研制出性能优异的大型干法水泥窑用直接结合镁铬砖LZMGe-8A。
补充资料：镁砖
分子式：
CAS号：
性质：氧化镁含量在90%以上、以方镁石为主晶相的碱性耐火材料。一般可分为烧结镁砖（又称烧成镁砖）和化学结合镁砖（又称不烧镁砖）两大类。纯度和烧成温度高的镁砖，由于方镁石晶粒直接接触，称为直接结合镁砖；用电熔镁砂为原料制成的砖称为电熔再结合镁砖。镁砖有较高的耐火度，很好的耐碱性渣性能，荷重软化开始温度高，但抗热震性能差。烧结镁砖以制砖镁砖为原料，经粉碎、配料、混练、成型后，在1550～1600℃的高温下烧成，高纯制品的烧成温度在1750℃以上。不浇镁砖是在镁砂中加入适当的化学结合剂，经混炼、成型、干燥而制成。主要用于炼钢碱性平炉、电炉炉底和炉墙，氧气转炉的永久衬，有色金属冶炼炉，高温隧道窑，煅烧镁砖和水泥回转窑内衬，加热炉的炉底和炉墙，玻璃窑蓄热室格子砖等。
CAS号：
性质：氧化镁含量在90%以上、以方镁石为主晶相的碱性耐火材料。一般可分为烧结镁砖（又称烧成镁砖）和化学结合镁砖（又称不烧镁砖）两大类。纯度和烧成温度高的镁砖，由于方镁石晶粒直接接触，称为直接结合镁砖；用电熔镁砂为原料制成的砖称为电熔再结合镁砖。镁砖有较高的耐火度，很好的耐碱性渣性能，荷重软化开始温度高，但抗热震性能差。烧结镁砖以制砖镁砖为原料，经粉碎、配料、混练、成型后，在1550～1600℃的高温下烧成，高纯制品的烧成温度在1750℃以上。不浇镁砖是在镁砂中加入适当的化学结合剂，经混炼、成型、干燥而制成。主要用于炼钢碱性平炉、电炉炉底和炉墙，氧气转炉的永久衬，有色金属冶炼炉，高温隧道窑，煅烧镁砖和水泥回转窑内衬，加热炉的炉底和炉墙，玻璃窑蓄热室格子砖等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条