1) burned-magnesia brick
烧成镁砖
1.
We found the reasons that a lot burned-magnesia brick is scrapped because of split by delve into the production technology.
通过对烧成镁砖生产工艺的深入研究,找到了烧成镁砖批量开裂报废的原因,并通过一系列的试验工作,找到了解决方案,即通过加入"复合结合剂"来有效地杜绝制品烧后开裂现象,而且"复合结合剂"的加入没有降低制品的理化性能。
2) fired magnesia-calcium brick
烧成镁钙砖
1.
The production and application status of magnesite-dolomite refractories such as fired magnesia-calcium brick,unburned magnesia-calcium(carbon) brick and Mg-Ca coating mixture for tundish etc are introduced and it is pointed out that magnesite-dolomite refractories should be developed on high CaO content,high grade,seriation and non-shaped refractories in the near future.
介绍了我国烧成镁钙砖、不烧镁钙(碳)砖和镁钙质中间包涂料等镁钙质耐火材料的生产和使用现状,指出今后我国的镁钙质耐火材料应向高CaO含量、高档次、系列化和不定形方向发展。
3) chemical bonded magnesite brick
不烧镁砖
4) Fire magnesite-chrome brick
烧镁铬砖
5) Fired magnesite brick
烧镁砖
6) burned impregnated magnesodolomite brick
烧成油浸镁白云石砖
补充资料：镁砖
分子式：
CAS号：
性质：氧化镁含量在90%以上、以方镁石为主晶相的碱性耐火材料。一般可分为烧结镁砖（又称烧成镁砖）和化学结合镁砖（又称不烧镁砖）两大类。纯度和烧成温度高的镁砖，由于方镁石晶粒直接接触，称为直接结合镁砖；用电熔镁砂为原料制成的砖称为电熔再结合镁砖。镁砖有较高的耐火度，很好的耐碱性渣性能，荷重软化开始温度高，但抗热震性能差。烧结镁砖以制砖镁砖为原料，经粉碎、配料、混练、成型后，在1550～1600℃的高温下烧成，高纯制品的烧成温度在1750℃以上。不浇镁砖是在镁砂中加入适当的化学结合剂，经混炼、成型、干燥而制成。主要用于炼钢碱性平炉、电炉炉底和炉墙，氧气转炉的永久衬，有色金属冶炼炉，高温隧道窑，煅烧镁砖和水泥回转窑内衬，加热炉的炉底和炉墙，玻璃窑蓄热室格子砖等。
CAS号：
性质：氧化镁含量在90%以上、以方镁石为主晶相的碱性耐火材料。一般可分为烧结镁砖（又称烧成镁砖）和化学结合镁砖（又称不烧镁砖）两大类。纯度和烧成温度高的镁砖，由于方镁石晶粒直接接触，称为直接结合镁砖；用电熔镁砂为原料制成的砖称为电熔再结合镁砖。镁砖有较高的耐火度，很好的耐碱性渣性能，荷重软化开始温度高，但抗热震性能差。烧结镁砖以制砖镁砖为原料，经粉碎、配料、混练、成型后，在1550～1600℃的高温下烧成，高纯制品的烧成温度在1750℃以上。不浇镁砖是在镁砂中加入适当的化学结合剂，经混炼、成型、干燥而制成。主要用于炼钢碱性平炉、电炉炉底和炉墙，氧气转炉的永久衬，有色金属冶炼炉，高温隧道窑，煅烧镁砖和水泥回转窑内衬，加热炉的炉底和炉墙，玻璃窑蓄热室格子砖等。