1) PMMA/SiO_2
PMMA/SiO2
1.
PMMA/SiO_2 organic-inorganic hybrid sol was synthesized by monomer methyl methacrylate, 3- (triethoxysilyl)propylmethacrylate (mol ration is 1∶1), 0.
2 %(单体总量的质量分数 )的偶氮二异丁腈AIBN引发剂和四氢呋喃 (THF)溶剂 ,及 2 0 % (总质量分数 )的正硅酸乙酯TEOS合成出PMMA/SiO2 有机 无机杂化的杂化溶胶 。
2) PMMA/SiO_2 aerogel
PMMA/SiO2气凝胶
3) SiO2/PMMA composite particles
SiO2/PMMA复合粒子
1.
SiO2/PMMA composite particles were prepared by reverse atom transfer radical polymerization(RATRP).
采用反向原子转移自由基法,制备了SiO2/PMMA复合粒子。
4) PMMA/SiO2 composite microsphere
PMMA/SiO2复合微球
1.
PMMA/SiO2 composite microspheres with different morphologies were prepared via conventional emulsion polymerization with sodium dodecyl sulfate (SDS) or polyoxyethylene otyl phenyl ether (OP-40) as surfactant and 4-VP as the auxiliary monomer.
以4-乙烯基吡啶(4-VP)为辅助单体,分别使用十二烷基硫酸钠(SDS)和OP-40(CA897)作乳化剂,在SiO2存在下用常规乳液聚合合成了PMMA/SiO2复合微球。
5) PMMA/SiO 2 Hybrid quasi-gel
PMMA/SiO2杂化准凝胶
6) PMMA/SiO_(2) sol-gel composite glass
PMMA/SiO2溶胶-凝胶复合玻璃
补充资料：PC/PMMA blend
分子式：
CAS号：
性质：PC与PM-MA共混，一般采用机械共混法。该共混物的注塑成型工艺条件是：注塑前需在110～120℃下干燥几小时，注塑温度为240～260℃，若高于270℃易分解。模具温度60～80℃。与PC相比，共混材料具有如下特性：(1)抗冲击强度明显提高，可比PC高5～7倍；(2)耐应力开裂性可比PC高1.3～3倍；(3)耐沸水性有较大提高；(4)有美丽的珍珠光泽；(5)无毒；(6)基本上保持了PC的卓越机械性能和尺寸稳定性。适于制作化妆品、食品容器、汽车内部装饰件、建筑装饰材料等。