1) carbonaceous crystallite
碳质微晶
2) crystallitic carbon
微晶碳
1.
The crystallitic carbon was prepared from anthracite by demineralization and carbonization,then the magnesium/carbon nanocomposites for hydrogen storage were manufactured through reaction milling of the mixture of magnesium,crystallitic carbon and aluminium under hydrogen atmosphere.
将无烟煤进行脱灰和碳化,制备微晶碳,再将微晶碳和铝添加到镁中,用氢气反应球磨法制取镁/碳纳米复合储氢材料。
2.
The carbon/magnesium hydrogen storage materials were prepared by reaction ball milling under hydrogen atmosphere with Mg and crystallitic carbon which were made from anthracite, sponge coke and activated carbon after carbonization and pre-graphitization and using needle coke, deposited carbon from pyrolysis of acetylene as carbon raw materials.
本文将无烟煤、海绵焦和活性炭经950℃碳化,1500℃预石墨化处理制成微晶碳,以及以针状焦和乙炔热解沉积碳为碳原料,添加到金属Mg中,在氢气气氛下反应球磨制备碳镁储氢材料。
3) amorphous carbon
非晶质碳
4) carbon (carbonaceous) microribbon
碳(质)微带
5) microcrystal B_4C
微晶碳化硼
6) carbon microcrystallite size
碳微晶尺寸
补充资料：多孔碳晶须
分子式：
CAS号：
性质：具有多微孔表面的碳晶须。比表面积20.6m2/R，比表面积比2.1～17.8，弯曲强度和模量各为155～208MPa和5.7～6.3GPa。对树脂等基体具有良好的黏合性。制法是将直径0.8μm，平面形状比46，相对密度1.96和比表面积2.58m2/g的气相成长碳晶须，边加热至1000℃边与水蒸气和氮混合气接触而得。用于作塑料、陶瓷、金属和橡胶基复合材料增强剂及层间化合物的晶核等。
CAS号：
性质：具有多微孔表面的碳晶须。比表面积20.6m2/R，比表面积比2.1～17.8，弯曲强度和模量各为155～208MPa和5.7～6.3GPa。对树脂等基体具有良好的黏合性。制法是将直径0.8μm，平面形状比46，相对密度1.96和比表面积2.58m2/g的气相成长碳晶须，边加热至1000℃边与水蒸气和氮混合气接触而得。用于作塑料、陶瓷、金属和橡胶基复合材料增强剂及层间化合物的晶核等。