1) luminescence ceramics
发光陶瓷
1.
It is shown that the SrAl 2O 4 monolithic crystal structure was observed i n the SrAl 2O 4:Eu 2+ ,Dy 3+ luminescence ceramics, according to t he resulfs of X-rays diffraction.
用SrCO3 、Al2 O3 、Eu2 O3 和Dy2 O3 烧制SrAl2 O4:Eu2 + ,Dy3 + 长余辉光致发光陶瓷 ,其烧结温度为 1 30 0℃— 1 4 0 0℃ ,烧结时间为 3小时。
2) Shining ceramic glaze
发光陶瓷釉
3) multicolor luminescence ceramics
多彩发光陶瓷
4) Study on and Manufacture Luminescent Glaze Ceramics
发光陶瓷的研制
5) Ceramic Development
陶瓷发展
6) foaming ceramics
发泡陶瓷
1.
The result of experiments shows that under the pressure of 75 ～ 150kg/cm2, firing temperature of 1165 ～ 1175℃,short insulation time can produce foaming ceramics as major closed porosity, and uniform microstructure.
以抛光砖废渣和珍珠岩尾矿为基料,探讨成型压力对制备闭孔发泡陶瓷的影响,试验结果表明:为制备闭孔为主,显微结构均匀的发泡陶瓷,成型压力75-150kg/cm2,烧成温度1165℃-1175℃,短保温时间,是比较适宜的。
补充资料：场致发光材料(见电致发光材料)
场致发光材料(见电致发光材料)
electroluminescent material
见场致发光材料eleetrolumineseent material 电致发光材料。