1) clay atmometer
陶瓷蒸发计
2) dish ,evaporating, ceramic
陶瓷蒸发皿
3) luminescence ceramics
发光陶瓷
1.
It is shown that the SrAl 2O 4 monolithic crystal structure was observed i n the SrAl 2O 4:Eu 2+ ,Dy 3+ luminescence ceramics, according to t he resulfs of X-rays diffraction.
用SrCO3 、Al2 O3 、Eu2 O3 和Dy2 O3 烧制SrAl2 O4:Eu2 + ,Dy3 + 长余辉光致发光陶瓷 ,其烧结温度为 1 30 0℃— 1 4 0 0℃ ,烧结时间为 3小时。
4) Ceramic Development
陶瓷发展
5) foaming ceramics
发泡陶瓷
1.
The result of experiments shows that under the pressure of 75 ～ 150kg/cm2, firing temperature of 1165 ～ 1175℃,short insulation time can produce foaming ceramics as major closed porosity, and uniform microstructure.
以抛光砖废渣和珍珠岩尾矿为基料,探讨成型压力对制备闭孔发泡陶瓷的影响,试验结果表明:为制备闭孔为主,显微结构均匀的发泡陶瓷,成型压力75-150kg/cm2,烧成温度1165℃-1175℃,短保温时间,是比较适宜的。
6) ceramic design
陶瓷设计
1.
Chinese modern ceramic design education has undergone more than half a century, It trained numbers of ceramic professionals and appeared very active function in ceramic industry.
中国现代陶瓷设计教育走过了半个多世纪,培养了大批陶瓷专业人才,对发展陶瓷产业起到了非常积极的作用。
2.
Meanwhile what is the ceramic designer s eternal pursue is the unique form.
艺术贵在交流与创新,让造型装饰出新出奇、各具特色,是陶瓷设计者的永恒追求。
3.
Based on Chinese current teaching situation, describe the importance of the practice teaching in ceramic design education by three aspects include inspect ceramic-producing areas, establish cooperative projects with well-known ceramics enterprises and the establishment of practice base.
陶瓷设计教育对整个陶瓷业的发展起着重要的作用,但我国的陶瓷教育仍然存在很多问题。
补充资料：场致发光材料(见电致发光材料)
场致发光材料(见电致发光材料)
electroluminescent material
见场致发光材料eleetrolumineseent material 电致发光材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条