1) Water-cooled ingot mould
水冷锭模
2) Cold Ingot
冷锭
1.
Study on The Calculation Basis of a Heating Specification for Cold Ingots;
冷锭加热规范计算基准的研究
3) ingot mould
锭模
1.
This article tells of the necessarity of developing new ingot mould and the design of changing the bottom of ingot mould.
阐述了开发新型锭模的必要性和换底锭模的创新设计思路,扼要介绍了换底锭模的生产方法及其使用效果。
2.
The characteristics of bottom change-over ingot mould are introduced as well as the tests and the results comparing with former ingot mould.
介绍了换底锭模的特点及其与旧式锭模进行现场对比试验情况和结果,从设计、综合力学性能和冷却能力等方面对换底锭模寿命长、合金质量好的原因进行了定性和定量分析。
3.
The working conditions and properties requirements of moulds for aluminum ingot production,as well as the production technology of vermicular iron-made ingot mould was described.
介绍了铝锭模的工作条件、性能要求和蠕墨铸铁铝锭模的生产方法,比较了蠕黑铸铁、灰铸铁和球墨铸铁的静载力学性能、高温力学性能和耐热疲劳性能,认为蠕墨铸铁材料用作铝锭模材料较为合适。
4) ingot mold
锭模
1.
This paper studies the relationship between the rheological and technological properties of the coating for ferroalloy ingot mold.
研究了水基锭模耐火涂料的流变学性质与其工艺性能之间的关系。
5) Water-cooling in Cu Mould
水冷铜模
6) water-cooled mould
水冷模
补充资料：锭模涂料
锭模涂料
coating mixture
d ingmo tulioo锭模涂料(eoating mixture)以消除钢锭表面缺陷和减少钢锭模消耗为目的的钢锭模内表面涂敷剂。使用时将其用特殊的喷涂设备均匀地喷洒在钢锭模内表面上，在浇注过程中这层涂膜使钢锭的结疤、翻皮、裂纹、表面气泡和皮下气泡等多种表面缺陷得到极大的抑制。同时，它减少了钢锭焊模现象并阻止了钢水对锭模表面的侵蚀和冲刷，起到保护钢锭模的作用。此外，该涂层的隔热作用使钢锭的凝固时间相应延长，在某种程度上减少了钢锭缩孔的形成并相应延长了夹杂的上浮时间，有利于其排除。 锭模涂料分为两类:一类是模壁涂料，另一类是模底涂料。以往模壁涂料多以煤焦油、重油、石墨等为基体材料，由于其热分解温度与最佳值相差较大且会引起模壁残碳附着部位的渗碳严重，已被水溶性树脂所取代。水溶性树脂的作用机理是:当浇注时产生的飞溅液滴粘在涂有树脂的锭模上时，该层树脂在400~600℃的温度条件下会产生分解反应，释放出气体从而使得飞溅液滴凝固后自动脱落。研究表明，水溶性树脂分解残留物的高温勃度在1000~30。。cst之间时，钢锭的表面质量更加优异。另外，对钢锭模涂料还有一些附加的要求。一是导热系数低，与锭模有强的附着力，高温下最好能有一定的表面强度和抗急热性。模底涂料一般指底板涂料、底板修补剂和防漏剂。这类涂料多为硅质、铝质或镁质材料，不会污染钢水。多采用喷涂方式，有时也将其制成泥糊状以手工涂敷。 (尹弘斌)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。