3) epoxy resin/polyurethane
环氧树脂/聚氨酯
1.
he paper illustrates the analysis of some characteristics of the epoxy resin/polyurethane semi IPN, such as glass transtion behavior, damping and mechanical properties as well as morphology by the DMA (Dynamic Mechanical Analysis) method and SEM (Scanning Electron Mirroscope).
本文从分子水平上对环氧树脂／聚氨酯（ＥＰ／ＰＵ）互穿形成的半ＩＰＮ材料的玻璃化转变温度、阻尼性能、力学性能、表面与断口形态特征进行了微相结构分析。
4) polyurethane-epoxy resin
聚氨酯环氧树脂
1.
Adhesive properties of calcium sulfate whisker-modified polyurethane-epoxy resins;
硫酸钙晶须改性聚氨酯环氧树脂的粘接性能
5) low branched polyester epoxy
低度支化聚酯环氧树脂
1.
In order to obtain the epoxy with excellent heat-resistance,the low branched polyester epoxy(LBPE) was synthesized with 1,2,4-benzenetricarboxylic andydride,1,4-benzenedimethanol and 1-chloro-2,3-epoxypropene as raw materials,and the modified epoxy with LBPE in bisphenol-A epoxy was obtained in this paper.
为得到良好耐热性能的环氧树脂,以1,2,4-苯三酸酐(TMA)、1,4-苯二甲醇(PTA)和环氧氯丙烷(ECH)等为原料合成了低度支化聚酯环氧树脂(LBPE),并对该环氧改性双酚A环氧树脂,运用热变形温度(HDT)、动态热机械分析(DMA)和示差扫描量热(DSC)技术表征了改性环氧树脂的耐热性能。
补充资料：酚醛环氧乙烯基酯不饱和聚酯树脂
分子式：
CAS号：
性质：含有酚醛环氧甲基丙烯酸酯结构的不饱和聚酯树脂。较双酚A二缩水甘油醚(即双酚A环氧)型乙烯基酯聚酯交联密度大、热变形温度高、耐热性好，但可挠性和耐碱性稍差。多数性能基本相似。铸塑料热变形温度129℃。增强塑料的拉伸强度29.42MPa，拉伸模量17.16GPa，弯曲强度31.36MPa，弯曲模量14.7GPa，冲击强度86kJ/m2；体积电阻率5.41×1013Ω·cm，介电强度25.9MV/m。由苯酚、甲醛制成线型酚醛树脂后，再与甲基丙烯酸反应制得。可制作玻璃纤维增强塑料和铸塑料等用于耐高温、耐腐蚀和耐溶剂等方面的设备和零部件。
CAS号：
性质：含有酚醛环氧甲基丙烯酸酯结构的不饱和聚酯树脂。较双酚A二缩水甘油醚(即双酚A环氧)型乙烯基酯聚酯交联密度大、热变形温度高、耐热性好，但可挠性和耐碱性稍差。多数性能基本相似。铸塑料热变形温度129℃。增强塑料的拉伸强度29.42MPa，拉伸模量17.16GPa，弯曲强度31.36MPa，弯曲模量14.7GPa，冲击强度86kJ/m2；体积电阻率5.41×1013Ω·cm，介电强度25.9MV/m。由苯酚、甲醛制成线型酚醛树脂后，再与甲基丙烯酸反应制得。可制作玻璃纤维增强塑料和铸塑料等用于耐高温、耐腐蚀和耐溶剂等方面的设备和零部件。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条