3) quardrupedal crystal whisker of zinc oxide
四针状ZnO晶须
1.
The ultra high molecular weight polyethylene (UHMWPE) composites filled with superfine kaolin and quardrupedal crystal whisker of zinc oxide were prepared.
采用超细高岭土和四针状ZnO晶须对超高分子量聚乙烯 (UHMWPE)进行物理填充改性 ,研究了这 2种填料对于UHMWPE摩擦磨损性能的影响。
4) tetrapod-shaped nano-whisker
四针状纳米晶须
5) T-ZnOw
四针状氧化锌晶须
1.
The tetrapod-like zinc oxide whisker (T-ZnOw) is the sole tetrapod-like whisker in crystal whisker family, which has clear and neat three-dimensional space structure.
四针状氧化锌晶须 (T -ZnOw)是晶须家族中目前发现的唯一具有规整三维空间结构的四针状晶须。
2.
The surface of tetra-needle like zinc oxide whisker(T-ZnOw) was modified by silane coupling agent(KH-560) and titanate coupling agent(TM-38S).
采用硅烷偶联剂KH-560和钛酸酯偶联剂TM-38S对四针状氧化锌晶须(T-ZnOw)进行表面改性,制备了相应的聚苯硫醚(PPS)尼/龙(PA)66/T-ZnOw复合材料,研究了两种偶联剂及其复合体系对T-ZnOw表面改性效果和相应复合材料力学性能的影响,并利用扫描电子显微镜对复合材料的断面形态进行了观察。
3.
The microwave depleting mechanisms of tetra-needle like zinc oxides (T-ZnOw) have been discussed.
分析了四针状氧化锌晶须(T-ZnOw)的电磁波损耗机理,首先从T-ZnOw形成立体导电网及其感应涡流损耗和晶须内部散射电场计算等宏观角度讨论了入射电磁波损耗机制;其次,从针尖电荷集中和界面极化的角度分析了该晶须的电磁波损耗机理;最后,用量子力学的观点讨论了T-ZnOw与电磁波作用机理,发现隧道效应和量子势阱理论都可用于解释该晶须在2-18 GHz频率范围内的电磁波损耗。
6) tetrapod-shaped ZnO whisker
四针状氧化锌晶须
1.
In order to overcome the bad mechanical properties of traditional anti- static composites, Tetrapod-shaped ZnO whisker (T-ZnOw), a kind of semiconductor, was used as the antistatic filler and to enhance the mechanical properties of the composites profiting from its unique three dimensional needlelike shapes and its high modulus and strength.
为克服传统抗静电复合材料力学性能差的缺点,本课题采用半导体四针状氧化锌晶须(T-ZnOw)作为抗静电填料,利用其特有的三维四针状结构及较高的强度和模量来改善复合材料的力学性能。
补充资料：多晶莫来石晶须(纤维)
分子式：
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。