1) Fast heat-treatment process
快速烧成工艺
3) typical processes of rapid prototyping
快速成形工艺
1.
This paper introduces the rapid prototyping technology base on disperse/deposition formation method and analyses the characteristic of commercial typical processes of rapid prototyping,such as SL、LOM、FDM、SLS、TDP and so on.
介绍了基于离散 /堆积成形思想的快速成形技术 ,分析了SL、LOM、FDM、SLS、TDP等成功实现商业化的典型快速成形工艺各自的特点 ,并提出了快速成形设备选用时应注意的问题和应用快速成形技术的意义。
4) fast-firing
快速烧成
1.
The necessity and the development of ceramic fast-firing technology were briefly reviewed, temperature distribution at cross sections in fast-firing ceramic tunnel kiln was described, and concrete measures of temperature equilibrium at cross sections in fast-firing ceramic tunnel kiln were offered.
简要说明了陶瓷工业实现快速烧成的必要性及其发展状况,介绍了快烧陶瓷隧道窑各烧成阶段的截面温度分布情况,提出了均衡陶瓷快烧隧道窑截面温度的具体措施。
5) Fast firing
快速烧成
1.
The multi_component system R 2O(K 2O, Na 2O)-RO(CaO,MgO, ZnO)-Al 2O 3-B 2O 3-SiO 2 which fits for single fast firing cycle was adopted.
选择适合一次快速烧成的R2 O(K2 O ,Na2 O) -RO(CaO ,MgO ,ZnO) -Al2 O3-B2 O3-SiO2 系统 ,通过优化组成设计及物理化学过程的控制 ,实现了釉的自生分相乳浊 。
2.
The multi component system R 2O(K 2O,Na 2O) RO(CaO,MgO,ZnO)-Al 2O 3-B 2O 3 - SiO 2 which contains wide practical liquid liquid immiscibility region and fits for single fast firing cycle was adopted.
本研究选择具有大范围实用分相区、适合快速烧成的R2 O(K2 O ,Na2 O) -RO(CaO ,MgO ,ZnO) -Al2 O3-B2 O3-SiO2 系统 ,研究了该多元系统全熔块乳浊釉组成与结构间的相互关系。
6) quick technique
快速工艺
补充资料：快速烧成
分子式：
CAS号：
性质：指制品的烧成周期从传统的数十小时缩短为数小时，数十分钟，甚至数分钟的迅速烧成。为了实现快速烧成，在工艺上:严格控制入窑水分，尽量减少坯体线收缩率，采用双面加热坯体，减少其自身的温差，合理控制烧成等措施。在窑炉上可采用小断面隔焰窑，使用高速等温烧嘴，进行急冷和强制通风，采用轻质材料筑窑。快速烧成可用于坯体的素烧和釉烧。其优点是生产效率高，燃料消耗少。如采用微波烧结等新技术，烧成周期将大大缩短，实现快速烧成则更为容易。
CAS号：
性质：指制品的烧成周期从传统的数十小时缩短为数小时，数十分钟，甚至数分钟的迅速烧成。为了实现快速烧成，在工艺上:严格控制入窑水分，尽量减少坯体线收缩率，采用双面加热坯体，减少其自身的温差，合理控制烧成等措施。在窑炉上可采用小断面隔焰窑，使用高速等温烧嘴，进行急冷和强制通风，采用轻质材料筑窑。快速烧成可用于坯体的素烧和釉烧。其优点是生产效率高，燃料消耗少。如采用微波烧结等新技术，烧成周期将大大缩短，实现快速烧成则更为容易。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。