1) mismatch
[英]['mɪsmætʃ] [美]['mɪs'mætʃ]
非匹配焊接接头
1.
Safety assessment of duplex stainless steel pipe mismatch welded joints with surface flaw;
含表面缺陷的双相不锈钢管道非匹配焊接接头的安全评定
2) welding material match
焊接匹配
1.
Constant load tensile test was adopted to study the influence of welding material match and alloy element content on SSCC(sulfide stress corrosion cracking) of domestic pipeline steels.
结果表明:焊接匹配、合金元素是影响国产管线钢SSCC的重要因素。
3) matching welded joint
匹配接头
1.
This paper presents a thorough study of the effect of groove shapes X & V on the mechanical properties of the different matching welded joints, including impact toughness, hardness and tensile strength.
引入匹配比的概念，提出了由匹配接头理论匹配比计算实际匹配比的简化计算公式以及接头实际匹配状态的判据，从而对上述影响规律予以定量化。
4) welding matching
焊接匹配性
5) undermatching welding
低匹配焊接
1.
Research and application of undermatching welding for 900 MPa high strength steel
900MPa高强钢低匹配焊接研究及应用
6) slip line field
低匹配接头
1.
Appraisement on the load-bearing ability of undermatching welded joint using slip line field method;
用滑移线场方法评价低匹配接头的承载能力
补充资料：焊接接头晶间腐蚀
焊接接头晶间腐蚀
welded joint intercryctalline corrosion
honjle」}etou jingj旧n fush{焊接接头晶间腐蚀(welded joint intererys-talline eorrosion)在焊接接头处出现的沿晶粒边界发生的腐蚀现象。外观仍可有金属光泽，但实际上晶粒已失去联系，钢质已变脆。在奥氏体不锈钢部位有焊缝晶间腐蚀、敏化区腐蚀和刀状腐蚀等三种不同部位的晶间腐蚀。关于奥氏体不锈钢的晶间腐蚀机理有多种学说，其中以碳化物(如er23e。或(er、Fe)23e。等)在晶界沉淀现象的“贫铬理论”比较为人们所接受。所以为防止这类晶间腐蚀尽量降低含碳量，使焊缝金属含有一定量的稳定元素(如钦、妮等)以防止或降低晶界Cr23C。的形成。此外，焊缝的组织状态也有影响，单相奥氏体组织的焊缝有利于柱状晶的发达，出现贫铬层后会使腐蚀贯穿于晶粒之间，若焊缝为奥氏体了加高温铁素体占的双相组织，由于树枝状被打破，不能构成集中的腐蚀通道。高铬铁素体也会有晶间腐蚀，但与奥氏体钢不同的是从高温急冷下来即有晶间腐蚀倾向，可通过650一85oC加热、缓冷使铬扩散均匀化来消除贫铬层，防止晶间腐蚀。 (许祖泽)