1) cleavage fracture
解理断口
1.
And with the increasing of temperature,fracture mode varied significantly from cleavage fracture to ductile fracture.
5 %Si Fe热轧合金的层状组织消除 ;其断裂模式随拉伸温度的升高迅速由解理断裂向韧性断裂转变 ;在 2 0 0℃拉伸时 ,为纯解理断口 ,此时该合金即具有高达 2 6 %的延伸率 ;但是在 2 0 0℃ - 40 0℃温区 ,延伸率未随温度的升高而显著增大 ,其断口形貌为解理 +韧窝的混合断口 ;在 5 0 0℃拉伸时 ,为纯韧窝断口 ,其延伸率可达 43
2.
The cleavage fracture surfaces of Ti_3Al and Ti-24Al-11Nb samples after tensile tests in air were studied with a scanning tunnel microscope(STM).
采用隧道扫描显微镜（ＳＴＭ）对Ｔｉ３Ａｌ及Ｔｉ－２４Ａｌ－１１Ｎｂ试样在空气中拉伸的解理断口进行了研究。
2) quasi-cleavage fracture
准解理断口
3) cleavage fracture
劈裂，解理断口
4) hydrogen-embrittlement induced
氢致准解理断口
5) cleavage fracture
解理断裂
1.
Influence of loading rate on critical event of cleavage fracture in notched specimen of low alloy steel;
加载速度对低合金钢缺口试样解理断裂临界事件的影响
2.
Hard brittle particles can have an important influence on cleavage fracture in steels, and can act as cleavage initiators.
钢中的脆硬粒子对钢的解理脆断有直接的影响 ,解理断裂源大都发生在脆硬粒子上 。
3.
The results show that before a critical load is reached, the crack tip is blunted only and in its vicinity the three criteria of cleavage fracture are satisfied in different regions separated from each other.
研究结果表明:在达到某一临界载荷前,裂尖只发生简单的钝化,并且在裂尖前端满足解理断裂三个判据的不同区域是相互分离的。
6) critical comprehension
评断理解
补充资料：解理
分子式：
分子量：
CAS号：
性质：又称劈开。矿物晶体受外力作用沿一定方向裂开在光滑面的性质。解理的难易，决定于晶体的内部结构。一般可将解理的完善程度分为五级：（1）极完全解理。解理面很平滑，裂成层片很薄，极不容易发生断口。例如云母。（2）完全解理。解理面常平滑，往往可沿解理而裂开成外形与原来晶形相像的小块，不容易发生断口。例如方解石。（3）中等解理。在碎块上可看到解理面和不定方向的断口。例如正长石。（4）不完全解理。碎块中可看到解理面，但比较困难。断口常是不平整的表面。例如磷灰石。（5）极不完全解理。碎块表现出断口。实际上没有解理，只在偶然的场合才能发现解理。例如石英。
分子量：
CAS号：
性质：又称劈开。矿物晶体受外力作用沿一定方向裂开在光滑面的性质。解理的难易，决定于晶体的内部结构。一般可将解理的完善程度分为五级：（1）极完全解理。解理面很平滑，裂成层片很薄，极不容易发生断口。例如云母。（2）完全解理。解理面常平滑，往往可沿解理而裂开成外形与原来晶形相像的小块，不容易发生断口。例如方解石。（3）中等解理。在碎块上可看到解理面和不定方向的断口。例如正长石。（4）不完全解理。碎块中可看到解理面，但比较困难。断口常是不平整的表面。例如磷灰石。（5）极不完全解理。碎块表现出断口。实际上没有解理，只在偶然的场合才能发现解理。例如石英。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条