1) Ti-Ni Inter-metallic compound
钛镍金属间化合物
2) Ni 3(SiAl)
镍三硅铝金属间化合物
3) Fe-Ni-Zn intermetallic compound
铁镍锌金属间化合物
1.
In this thesis, the reaction between low carbon steel containing Si and liquid Zn or Zn-Ni alloy, the formation and the growth kinetics of Fe-Zn and Fe-Ni-Zn intermetallic compounds are studied.
本文研究了含硅低碳钢与液态锌及锌镍合金的反应,铁锌和铁镍锌金属间化合物相层的形成过程及生长动力学规律,含硅低碳钢中的硅和锌浴中的镍对金属间化合物相层生长的影响;研究了各种锌渣相的成分、相结构及其形成机制;采用预镀镍的方法,研究了含硅低碳钢预镀镍后与液态锌的反应以及金属间化合物组织的形成和变化规律。
4) Ti-Al intermetallic
钛铝金属间化合物
1.
Ti-Al intermetallic matrix composite with interpenetrating Al2O3 whiskers was fabricated in situ through heat-treating the prefabricated pieces consisting of titanium,aluminum and external reactant powders at partial-oxidizing atmosphere.
以金属钛粉、铝粉及添加剂为原料压制成预制体,通过石墨与氧化铝混合粉对预制体的覆埋实现气氛保护并进行热处理,使其原位合成氧化铝纤维增强钛铝金属间化合物复合材料。
2.
Ti-Al intermetallic matrix composite with interpenetrating Al2O3 whiskers w as fabricated in-situ by heat-treating the prefabricated pieces consisted of titanium, aluminum and columbium pentoxide powder in non-oxidizing atmospher e.
以金属钛粉、铝粉和五氧化二铌粉末压制成预制体,通过石墨与氧化铝混合粉对预制体的覆埋实现气氛保护并进行热处理,使其发生化学反应原位合成氧化铝晶须增韧钛铝金属间化合物复合材料。
5) Ti-Si intermetallic compound
钛硅金属间化合物
6) nitinol
['nitinɔl,'nai-]
镍钛金属互化物<能>
补充资料：钛铝金属间化合物
分子式：
CAS号：
性质：钛铝原子比为1：1的金属间化合物。为以面心立方晶格为基础的L10型有序结构。密度小，为3.91g/cm3。使用温度达1000℃。具有良好的高温比强度和比刚度。优异的抗氧化性能。可采用高温合金的制备方法制取。理想的航天航空用轻量型高温材料。
CAS号：
性质：钛铝原子比为1：1的金属间化合物。为以面心立方晶格为基础的L10型有序结构。密度小，为3.91g/cm3。使用温度达1000℃。具有良好的高温比强度和比刚度。优异的抗氧化性能。可采用高温合金的制备方法制取。理想的航天航空用轻量型高温材料。