1) ultrasonic spray pyrolysis
超声喷雾热解
1.
In this paper SnO 2:F thin films were deposited by ultrasonic spray pyrolysis technology.
本文在超声喷雾热解成膜技术基础上 ,对沉积装置进行了改进 ,同时对反应液配方进行了优化 ,在较低温度制备出透明 Sn O2 :F导电薄膜。
2) ultrasonic spray pyrolysis
超声喷雾热分解
1.
SnO_2 thin film by ultrasonic spray pyrolysis;
用超声喷雾热分解法制备二氧化锡薄膜
2.
Spherical morphology LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2 as a cathode material of lithium ion batteries was successfully synthesized by an ultrasonic spray pyrolysis method.
采用超声喷雾热分解工艺合成了球形锂离子电池正极材料LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2。
3.
Ag doped ZnO films(ZnO:Ag) were deposited on quartz glass substrates by ultrasonic spray pyrolysis technology.
采用超声喷雾热分解法在石英衬底上以醋酸锌水溶液为前驱体,以硝酸银水溶液为Ag掺杂源生长了Ag掺杂ZnO(ZnO:Ag)薄膜。
3) ultrasonic spray pyrolysis
超声喷雾热解法
1.
27) thin films, with no phase separation and good crystallinity, were deposited on Si(100) and quartz glass substrates by ultrasonic spray pyrolysis (USP) technology.
采用超声喷雾热解法,在Si(100)和石英玻璃衬底上,生长出没有相偏析、结晶质量好、不同组分比的Zn1-xMgxO薄膜(x=0。
4) ultrasonic spray pyrolysis(USP)
超声喷雾热解(USP)
1.
ZnO thin films were grown on glass substrate by ultrasonic spray pyrolysis(USP) under different substrate temperatures.
利用超声喷雾热解(USP)技术,以普通玻璃为衬底,制备了不同衬底温度下的系列ZnO薄膜。
5) ultrasonic spray pyrolysis
超声喷雾热分解法
1.
Preparation of SnO_2: F thin films by ultrasonic spray pyrolysis;
用超声喷雾热分解法制备SnO_2:F薄膜
6) Pyrosol deposition
超声雾化喷涂热解
补充资料：废物热解
分子式：
CAS号：
性质：是在缺氧或无氧条件下废物的热分解过程。热解温度为500～800℃，比焚烧温度低。有机废物的热解可得到能分离、回收和再利用的气体或液体燃料。另外，由于热解温度相对较低，因此热解过程产生的氮氧化物(NOχ)少，而且尾气排放量也少。目前，发达国家已有城市垃圾、废塑料和废轮胎热解处理的工业化装置，但成功运行的这类工业化装置毕竟还很少，因此从总体来说，废物热解技术尚处在试验性生产的中试阶段。
CAS号：
性质：是在缺氧或无氧条件下废物的热分解过程。热解温度为500～800℃，比焚烧温度低。有机废物的热解可得到能分离、回收和再利用的气体或液体燃料。另外，由于热解温度相对较低，因此热解过程产生的氮氧化物(NOχ)少，而且尾气排放量也少。目前，发达国家已有城市垃圾、废塑料和废轮胎热解处理的工业化装置，但成功运行的这类工业化装置毕竟还很少，因此从总体来说，废物热解技术尚处在试验性生产的中试阶段。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条