1) alinite
阿利尼特
1.
Study on the Early Hydration Product of Alinite Cement;
阿利尼特水泥早期水化产物的研究
2.
By uaing technology of low temperature and salt solution, the author explores the feasibility of sintering the clinker alinite white cement at 12 000 ℃ .
利用低温盐溶工艺 ,探讨在 1 2 0 0℃烧成阿利尼特白水泥熟料的可行性 。
3.
The results show that the optimum burning temperature of the cement is in range of 1200—1350℃ and the composition of cement mineral is alinite with few C 11 A 7·CaCl 2.
研究结果表明 :该白水泥适宜煅烧温度范围为 12 0 0～ 13 5 0℃ ,形成的主要矿物为阿利尼特和少量C1 1 A7·CaCl2 ,随着温度的升高 ,C1 1 A7·CaCl2 逐渐减少 ,在 14 0 0℃ ,阿利尼特开始分解 ,形成了少量的C3S ;在 13 5 0℃下烧成熟料中 ,阿利尼特矿物质为不规则的多面体 ,表面带有平行晶纹 ;熟料为含有大量孔的烧结体 ,烧结体呈三维网络状结构。
2) alinite cement
阿利尼特水泥
1.
The hydraulic properties,mechanical properties and energy-saving characteristic of alinite cement are sum- rnarized.
阿利尼特水泥是一种节能水泥。
2.
The influence of gypsum on the forming of early hydrated product of new white alinite cement added gypsum was studied by means of DTA, XRD and SEM .
利用DTA,XRD,SEM等方法,研究了石膏对新型白色阿利尼特水泥的早期水化产物形成的影响。
3.
Municipal solid waste incinerator (MSWI) fly ash was successfully used as raw material in sintering alinite cement clinker in the laboratory.
以城市垃圾焚烧飞灰(以下简称焚烧飞灰)为主要原料,在实验室电炉里成功烧成了阿利尼特水泥熟料,分析了熟料烧成所需适宜的生料组成和最佳煅烧温度,并研究了石膏掺量对阿利尼特水泥强度影响,以及阿利尼特水泥的标准稠度用水量和凝结时间。
3) anileridine
阿尼利定
4) A.A.Anikst
阿·阿·阿尼克斯特
5) Modiliani
莫迪利阿尼
1.
Modiliani the end of the 19th century and early 20th century par is school one of the main representatives.
莫迪利阿尼是19世纪末20世纪初巴黎画派的主要代表人物之一。
6) anilipyrine
阿尼利匹林
补充资料：切利尼
| 切利尼（1500～1571） Cellini，Benvenuto 意大利雕刻家。1500年11月1日生于佛罗伦萨，卒于同地。从学习金银工艺进入艺坛。在艺术上倾慕米开朗琪罗，在风格上力求标新立异，是样式主义代表人物。主要作品《俄耳修斯》是一高3.2米的青铜雕像，技艺精熟，神情冷漠。切利尼一生游历甚广，性情暴烈，放荡不羁，晚年写《自传》历述生平，反映了时代精神。 |
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条