1) Sulfonated syndiotactic polystyrene
磺化间规聚苯乙烯
1.
The preparation of novel syndiotactic polystyrene/polyamide6/sulfonated syndiotactic polystyrene/montmorillonite (sPS/PA6/SsPS/MTA) nanocomposite by a meltintercalationblend process was proposed.
以磺化间规聚苯乙烯(SsPS)为增容剂,将间规聚苯乙烯(sPS)和尼龙6/改性蒙脱土纳米复合物(PA6 MTA)共混,得到综合性能优良的新型多组分聚合物/蒙脱土纳米复合材料(sPS/PA6/SsPS/MTA)。
2) potassium salt of sulfonated syndiotactic polystyrene ionomer
磺化间规聚苯乙烯钾盐
3) zinc salt of sulfonated syndiotactic polystyrene ionomer
磺化间规聚苯乙烯锌盐
1.
The syndiotactic polystyrene (sPS)/ polyethylene terephthalate (PET) composite was modified with montmorillonite(MMT) as reinforcing agent and zinc salt of sulfonated syndiotactic polystyrene ionomer as compatibilizer.
以蒙脱土(MMT)为增强剂、磺化间规聚苯乙烯锌盐(SsPS Zn)为增容剂来改性间规聚苯乙烯(sPS)/聚对苯二甲酸乙二酯(PET)复合材料,复合材料的综合力学性能和耐热性较未填充MMT时显著提高。
4) Zinc salt of sulfonated syndiotactic polystyrene (SsPSZn)
磺化间规聚苯乙烯锌盐(SsPSZn)
5) sulfonated polystyrene
磺化聚苯乙烯
1.
The sulfonated polystyrene (SPS) has been prepared by sulfonation reaction of the polystyrene, which is used as a filtrate reducer for oil well cement slurry.
通过磺化改性,制备了磺化聚苯乙烯(SPS)作为油井水泥降失水剂。
2.
Water borne emulsions of lightly sulfonated polystyrene ionomer(SPS) were prepared by phase inversion technique.
将聚苯乙烯磺化制成聚苯乙烯离聚体 (SPS) ,利用相反转技术 ,将磺化聚苯乙烯离聚体制成具有纳米级稳定的水基微乳液 ,利用 SPS微粒核为反应场所 ,引发另一单体 MMA聚合 ,制备具有相互缠结结构的 PMMA/ SPS复合水基微乳液。
3.
The complexation behavior of sulfonated polystyrene (SPS) containing 9.
采用粘度，差示扫描量热法研究了磺化聚苯乙烯（ＳＰＳ）与甲基丙烯酸甲酯－４－乙烯基吡啶共聚物（ＭＭＡ４ＶＰ）所形成的离子复合物。
6) SPS
磺化聚苯乙烯
1.
In this work, the polystyrene was modified to sulfonated polystyrene ionomer(SPS) and was emulsified to a stable polymer waterborne emulsion by using the technology of phase inversion.
将聚苯乙烯制成磺化聚苯乙烯离聚体,利用相反转技术,将磺化聚苯乙烯离聚体制成具有纳米级稳定的水基微乳液,利用磺化聚苯乙烯颗粒内部作为反应场所,引发另一单体丙烯酸丁酯聚合,制备聚丙烯酸丁酯/磺化聚苯乙烯复合水基微乳液。
2.
The polystyrene was modified to sulfonated polystyrene ionomer (SPS) which was emulsified to waterborne emulsion by using the technology of phase inversion.
利用相反转技术制备磺化聚苯乙烯(SPS)水基微乳液,研究发现,通过选择溶剂和控制混合溶剂的组成,可制备不同颗粒形态结构的SPS水基微乳液,并研究了相反转过程、乳液稳定性与混合溶剂组成之间的关系。
3.
he morphology and thermal property of sulfonated polystyrene (SPS) and its ionomers were studied through DSC, DMA, TEM, SAXS and TGA.
通过ＤＳＣ、ＤＭＡ、ＴＥＭ、ＳＡＸＳ和ＴＧ对ＳＰＳ（磺化聚苯乙烯）及其离聚体的形态结构和热性能进行了研究。
补充资料：间规聚苯乙烯
分子式：
CAS号：
性质： 系在其大分子碳-碳主链上苯基有规则交替排列在两侧的一种结晶型苯乙烯聚合物。为一种新型透明、耐热、高电绝缘性工程塑料。熔点266℃，密度1.01g/ml，拉伸强度35MPa，弯曲模量2550MPa，热变形温度95℃(1.82MPa应力下)，介质损耗正切0.001(1mHz)。结晶速度快。常呈现多种不同晶型和晶型转变。由苯乙烯在茂金属催化剂存在下聚合制得。用作电子、电器、汽车工业用注塑件，电容器薄膜，纤维过滤元件等。
CAS号：
性质： 系在其大分子碳-碳主链上苯基有规则交替排列在两侧的一种结晶型苯乙烯聚合物。为一种新型透明、耐热、高电绝缘性工程塑料。熔点266℃，密度1.01g/ml，拉伸强度35MPa，弯曲模量2550MPa，热变形温度95℃(1.82MPa应力下)，介质损耗正切0.001(1mHz)。结晶速度快。常呈现多种不同晶型和晶型转变。由苯乙烯在茂金属催化剂存在下聚合制得。用作电子、电器、汽车工业用注塑件，电容器薄膜，纤维过滤元件等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。