1) melt supercooled
熔体急冷
1.
These faces grow so rapidly that they have priority to appear and retain as the melt supercooled.
{ 3 2 1 }面族、{ 2 1 1 }面族和 { 1 1 1 }面族都是按 [GeO4]4-四面体以顶角相连的化学键链生长发育的 ,生长速度快 ,优先显露 ,在熔体急冷时保留下来。
2) melt-sharp cooling method
熔融-急冷法
3) Fuse-quench process
熔化急冷法
4) undercooled melt
过冷熔体
1.
Based on the physical processes of solute diffusion and interfacial energy, a model to describe free dendrite growth in undercooled melt was developed, including the effects of concentration undercooling, curvature undercooling and anisotropy of interfacial energy.
基于溶质扩散和界面能的作用,建立了过冷熔体中自由树枝晶的生长模型,考虑了成分过冷、曲率过冷和界面能各向异性。
2.
After the raw material of benzophenone was rectified by using distillation method,single crystal of benzophenone with dimension of about 30mm×40mm×60mm was grown with undercooled melt growth method.
本文采用过冷熔体法进行二苯甲酮晶体的生长实验 ,得到尺寸约为 30mm× 40mm× 6 0mm的单晶。
3.
Based on a phase-field model,a series of numerical calculations of dendritic growth into undercooled melt for a pure material were performed,and the influence of some physical parameters,including anisotropy strength,undercooling and noise factor,on dendritic growth were investigated.
利用相场法模拟纯物质过冷熔体中的枝晶生长过程,研究各向异性强度、过冷度、扰动等对枝晶生长的影响。
补充资料：耐急冷急热性
分子式：
CAS号：
性质：又称耐急冷急热性，耐热崩裂性，耐热冲击性。耐火材料抵抗温度的急变而不破坏的性能叫耐热震性。当制品突然受热（或受冷）发生膨胀（或收缩）时，由于其各部分的变形互相受到制约而产生热应力。当这种热应力超过制品内部的结合力时，制品就产生崩裂或剥落而破坏。耐火制品的耐热震性以实验方法测定。制品的耐热震性除受传递条件影响外主要取决于其热膨胀性、导热性、断裂韧性等，同时也与其组织结构、形状和尺寸等有关。为了防止耐火材料在使用时，因温度急变而引起崩裂，要求耐火材料具有良好的耐热震性。
CAS号：
性质：又称耐急冷急热性，耐热崩裂性，耐热冲击性。耐火材料抵抗温度的急变而不破坏的性能叫耐热震性。当制品突然受热（或受冷）发生膨胀（或收缩）时，由于其各部分的变形互相受到制约而产生热应力。当这种热应力超过制品内部的结合力时，制品就产生崩裂或剥落而破坏。耐火制品的耐热震性以实验方法测定。制品的耐热震性除受传递条件影响外主要取决于其热膨胀性、导热性、断裂韧性等，同时也与其组织结构、形状和尺寸等有关。为了防止耐火材料在使用时，因温度急变而引起崩裂，要求耐火材料具有良好的耐热震性。