1) NiAl(Cr,Nb) intermetallic
NiAl(Cr,Nb)金属间化合物
2) NiAl-Ta-Cr intermetallic compound
NiAl-Ta-Cr金属间化合物
3) NiAl intermetallic
NiAl金属间化合物
1.
The mechanical performance,alloying of NiAl intermetallic compound and methods for improving the combination of strength and toughness were summarized especially for the electric-thermal explosion directional spraying technology applied to form sub-micron grain NiAl intermetallic compound in situ and the composite coating.
综述了NiAl金属间化合物的力学性能、合金化以及提高强韧性的方法,并对NiAl合金的制备方法作了介绍,特别是利用电热爆炸超高速定向喷涂技术可原位生成亚微米晶NiAl金属间化合物及金属间化合物复合涂层。
2.
With the use of X-ray diffraction, SEM and EDS, the effect of iron element on the formation of NiAl intermetallic light beam surfacing layer and its microstructure were investigated.
采用X射线衍射、SEM、EDS等分析方法,研究了铁元素对光束堆焊合成NiAl金属间化合物层的成形和组织结构的影响规律。
4) NiAl intermetallics
NiAl金属间化合物
1.
NiAl intermetallics powder was compounded by the method of mechanical alloying and its ball milling process was discussed.
本文中用机械合金化法合成了NiAl金属间化合物粉末,详细介绍了球磨工艺,对NiAl金属间化合物粉末的形貌和物相进行表征。
2.
The NiAl intermetallics powders prepared by mechanical alloying were sintered by the spark plasma sintering.
通过脉冲放电等离子烧结技术对经机械合金化法合成的NiAl金属间化合物粉末进行了烧结,研究了NiAl金属间化合物的微观组织和力学性能。
补充资料：NiAl基金属间化合物高温合金
NiAl基金属间化合物高温合金
NiAl-base intermetallic compound superalloy
N一A IJ一]一nshuJ一an huohewu gaowen heJ旧NIAI基金属间化合物高温合金(NIAI一baseintermetallie eompound superalloy)以NIAI相为基体的金属间化合物高温合金。NIAI合金为体心立方BZ晶体结构.与Ni3AI合金相比，熔点高、密度小、具有更好的抗氧化性。但用作高温结构材料有两点不足:抗高温蠕变性能太差;室温脆性尚未得到根本解决。提高强度主要通过添加高熔点合金元素的固溶强化或者第二相质点的弥散强化(见高温合金强化)。添加铁可以形成两相组织，能提高屈服强度。通过机械合金化工艺加入第二相质点(Y刃3，TIBZ)也可以提高强度。最近，改善塑性的研究已得到令人鼓舞的结果，通过调整含铝量使之偏离正常成分而处在亚当量范围，获得y+丫两相组织(见高温合金材料的金属间化合物相)，可使N;AI基金属间化合物高温合金的室温拉伸塑性提高到5%~6%。 (邹敦叙)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条