1) Medium chromium white cast iron
中铬白口铸铁
1.
： The Stracture and properties of medium chromium white cast iron which was cooled in different modes after 40% hot deformation are observed,measured and analyzed.
对经４０％热变形后不同方式冷却的中铬白口铸铁的组织与性能进行观察与测试，并对其进行分析，所得结果对热变形中铬白口铸铁的应用具有重要的指导意义。
2.
The microstructure of medium chromium white cast iron with 6% vanadium was observed and analyzed by use of SEM and TEM.
采用扫描电镜(SEM)、透射电镜(TEM)对含钒6%的中铬白口铸铁的组织进行了分析,采用恒电流电解的方法提取了铸铁中的碳化物相,用XRD进行了物相分析,分析得出含钒中铬白口铸铁组织中的共晶碳化物为M_7C_3型碳化物,而弥散分布的黑色颗粒是MC型碳化物。
3) forged medium-chromium ally white cast iron
锻造中铬合金白口铸铁
4) medium-chromium abrasion-resistant cast iron
中铬抗磨白口铸铁
5) medium-Cr cast iorn
中铬白口铁
6) high chromium cast iron
高铬白口铸铁
1.
The effects of cryogenic treatment on the microstructure and the hardening behavior for high chromium cast iron were investigated by X-ray diffraction,magnetic method and hardness test.
采用X射线衍射、磁性法和硬度测量等方法研究了深冷处理对高铬白口铸铁显微组织和硬化行为的影响。
2.
In this paper, the influenceof remelt and insulation during the secondremelt on the carbide structural in- heritance of high chromium cast iron were studied.
采取重熔的工艺措施并在第二次重熔时进行保温处理,研究高铬白口铸铁中碳化物的遗传性并对高铬白口铸铁的力学性能进行测试。
补充资料：白口铸铁
在结晶凝固过程中没有石墨析出，断口呈银白色的铸铁。它含有较多的游离渗碳体，所以具有很高的硬度（一般在HB 500以上），但性脆。多用于抗磨损的零件，例如农具、磨球、磨煤机零件、抛丸叶片、泥浆泵零件、铸砂管以及冷硬轧辊的外表层等。以含碳量2.6～3.8％、含硅量0.6～0.9％、含锰量0.2～0.8％的铁水，加快铸件凝固过程，或加入强烈形成碳化物的金属元素的方法，可得白口铸铁件。中国早在春秋晚期已经使用白口铸铁（见冶金史）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。