1) SiC_p / Mahle142 matrix composites
SiCp/Mahle142复合材料
3) SiCp/LY12 composite
SiCp/LY12复合材料
1.
Resistance to plastic deformation (σp) in a range of 10~5~2×10~3 of plastic strain was investigated experimentally for a 35%SiCp/LY12 composite and its matrix alloy.
对SiCp/LY12复合材料及其基体LY12合金在10~(-5)～2×10~(-3)塑性应变范围内的塑变抗力进行了比较研究。
4) SiCp/Al MMCs
SiCp/Al基复合材料
1.
In order to analyze the weldability of SiC particle reinforced aluminum metal matrix composites(SiCp/Al MMCs),plasma arc in-situ welding of SiCp/Al MMCs was carried out using argon-nitrogen mixture as plasma gas with Ti-Mg mixed powder as in-situ material.
为分析SiCp/Al基复合材料的焊接性,以Ti-Mg混合粉末作为填充材料,采用氮氩混合等离子气体对SiCp/Al基复合材料进行等离子弧原位焊接。
2.
Plasma arc "in-situ" welding of SiCp/Al MMCs were carried out using argon-nitrogen mixture as plasma gases with Ti-Ni alloying as "in-situ" material.
以Ti-Ni合金作为填加材料,采用氮氩混合等离子气对SiCp/Al基复合材料进行等离子弧原位焊接。
3.
In this paper,SiCp/Al MMCs were selected as research objects,and process and mechanism of SiCp/6061Al MMCs by plasma arc welding(Ar and N2 as ionized gas, Ar as fielded gas) were systematically studied.
研究表明填加Al-Si-Ti-Ni合金对SiCp/Al基复合材料进行等离子弧原位焊接,填加材料中Ti含量为5%时,可以有效抑制有害相Al_4C_3的生成,得到的焊缝组织较为致密,没有气孔、微观裂纹等缺陷,接头强度较之不加填充材料时有较大提高,达到226MPa,提高了接头的力学性能。
5) SiCp/Al composites
SiCp/Al复合材料
1.
Preparation of high volume fraction SiCp/Al composites for electronic packaging;
电子封装用高体积分数SiCp／Al复合材料的制备
2.
Anti-corrosion properties of electroless nickel coating on SiCp/Al composites;
SiCp/Al复合材料化学镀镍耐蚀性研究
3.
An Application of Focusing Probe in SiCp/Al Composites′ Nondestructive Testing;
聚焦换能器在SiCp/Al复合材料超声无损检测中的应用
6) Al-Si/SiCp composite
Al-Si/SiCp复合材料
1.
The wear behaviors of spray deposited Al-Si/SiCp composites were investigated by using MM1000 frictional and wear testing machine.
通过MM1000摩擦磨损试验,研究了喷射沉积Al-Si/SiCp复合材料在干滑动状态下的摩擦磨损特征,并对摩擦层的显微组织和形貌进行了观察,同时对磨损机理进行了分析。