1) potassium tetratitanate
四钛酸钾
1.
The results indicate that potassium hexatitanate has better thermal stability than potassium tetratitanate.
结果表明:四钛酸钾(K2Ti4O9)的热稳定性低于六钛酸钾(K2Ti6O13)的。
2.
The test results indicate that meta-stable transformation of potassium tetratitanate begins at 950 ℃ or so,then finishes completely at higher than 1 100 ℃ and maintained for 2 h.
实验发现:在约950℃,四钛酸钾(K2Ti4O9)开始出现亚稳转变,1100℃以上保温2h后,其临界转变基本完成,说明K2Ti4O9是高温亚稳相,低于临界反应温度合成的六钛酸钾(K2Ti6O13)是由K2Ti4O9的亚稳相转变获得的。
2) potassium tetratitanate film
四钛酸钾薄膜
1.
A new nanosmooth potassium tetratitanate film was prepared on glass substrates by a sol-gel method using Ti(n-OC_4H_9)_4 and CH_3COOK as precursors.
在四钛酸钾薄膜上进行十八烷基三氯硅烷(OTS)的自组装,通过测量自组装单分子膜(SAMs)因光催化分解而导致接触角变化研究薄膜的光催化性能。
3) potassium tetratitanate fiber
四钛酸钾纤维
4) potassium tetratitanate(K2Ti4O9)whisker
四钛酸钾晶须(K2Ti4O9)
5) potassium tetratitanate whisker
四钛酸钾晶须
1.
Pre-concentration and separation of cadmium in environmental water with potassium tetratitanate whisker
四钛酸钾晶须预分离富集环境水样中镉
6) potassium titanate
钛酸钾
1.
Transesterification of DMC and EHOH over potassium titanate for synthesis of di-2-ethyl hexyl carbonate(DEHC);
钛酸钾催化DMC酯交换反应合成碳酸二异辛酯的研究
2.
KOH sub-molten salt method was studied for preparing potassium titanate whiskers and titanium dioxide by using titaniferous slag as the raw material.
研究了以高钛渣为原料、采用KOH亚熔盐法制备钛酸钾晶须和二氧化钛的新方法,探讨了反应温度、初始KOH浓度、反应时间和碱矿比等因素对钛酸钾晶须形貌的影响。
3.
This experiment adopts KOH alkali treatment, so as to appear in situ potassium titanate layer on titanium alloy surface, and form firm chemical bond equal to with titanium alloy matrix.
本实验采用KOH碱处理,以便在钛合金表面原位自生出钛酸钾层,并与钛合金基体形成牢固的化学键合。
补充资料：四碘合金(III)酸钾
分子式：KAuI4
CAS号：
性质：又名碘金酸钾。黑色闪光晶体。对光敏感。熔点150℃(分解)。溶于稀碘化钾溶液。在冷水中分解并释出碘。碘化金与碘化钾溶液作用而得。
CAS号：
性质：又名碘金酸钾。黑色闪光晶体。对光敏感。熔点150℃(分解)。溶于稀碘化钾溶液。在冷水中分解并释出碘。碘化金与碘化钾溶液作用而得。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条