1) potassium titanate whisker
钛酸钾晶须
1.
Preparation of PP vehicle materials Co-reinforced by the natural fiber and potassium titanate whisker;
苎麻纤维和钛酸钾晶须混杂增强聚丙稀车用材料的研制
2.
Preparation and properties of electroless composite plating of nickel-phosphous-potassium titanate whisker;
镍-磷-钛酸钾晶须化学复合镀层的制备及性能
3.
A study on the properties of the potassium titanate whiskers—PTFE composites;
钛酸钾晶须增强聚四氟乙烯复合材料性能的研究
2) potassium titanate whiskers
钛酸钾晶须
1.
Preparation and property of SiO_2-potassium titanate whiskers composite particles;
SiO_2钛酸钾晶须复合微粒的制备及性质研究
2.
Moisture absorbing ability and tribology capability of potassium titanate whiskers reinforced MC nylon;
钛酸钾晶须改性MC尼龙的吸湿行为及摩擦学特性
3.
Evaluate the effect of different heat-cure time on the flexural strength of the resins reinforced by potassium titanate whiskers
热处理时间对钛酸钾晶须增强牙用复合树脂的抗弯强度的影响
3) potassium titanate whiskers
六钛酸钾晶须
1.
The cost-effective potassium titanate whiskers are artificial fibers with high performance.
六钛酸钾晶须是一种高性能、多用途的合成纤维。
4) potassium hexatitanate whiskers
六钛酸钾晶须
1.
Calcination synthesis of potassium hexatitanate whiskers with low content of water soluble potassium ions;
烧结法制备含低水溶钾的六钛酸钾晶须
2.
Potassium hexatitanate whiskers were synthesized using TiO2 and K2CO3 as starting materials with KDC method(Kneading-Drying-Calcination).
5和2 h)对合成六钛酸钾晶须的影响,并对合成试样进行了XRD和SEM分析。
5) oct-potassium titanate whisker
聚八钛酸钾晶须
6) potassium tetratitanate(K2Ti4O9)whisker
四钛酸钾晶须(K2Ti4O9)
补充资料：钛酸钾纤维增强体
分子式：
CAS号：
性质：无机多晶纤维体。典型商品纤维的平均直径约1μm，长度约290μm，熔点1371℃，比表面积1lm2/g，理论密度3.68g/cm3，拉伸强度16GPa，初始模量2.75GPa，伸长率0.59％，具有较好的耐热性能。采用水热合成法、熔融盐培育法和烧成法等制取。用作防热和高温用绝缘功能复合材料和结构复合材料的增强纤维等。
CAS号：
性质：无机多晶纤维体。典型商品纤维的平均直径约1μm，长度约290μm，熔点1371℃，比表面积1lm2/g，理论密度3.68g/cm3，拉伸强度16GPa，初始模量2.75GPa，伸长率0.59％，具有较好的耐热性能。采用水热合成法、熔融盐培育法和烧成法等制取。用作防热和高温用绝缘功能复合材料和结构复合材料的增强纤维等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条